SABIC Innovative Plastics LNP THERMOCOMP MF006SXP PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP MF006SXP PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* MF006SXP is a compound based on Polypropylene resin containing 30% Glass Fiber. Added features of this material include: Chemically Coupled.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 |
| 1.134 g/cc | 0.04097 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.0200 % | 0.0200 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0300 % | 0.0300 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0096 cm/cm @Time 86400 sec |
0.0096 in/in @Time 24.0 hour |
ISO 294 |
| 0.010 cm/cm @Time 86400 sec |
0.010 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 88.0 MPa | 12800 psi | ASTM D638 |
| 91.0 MPa | 13200 psi | ISO 527 | |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| 3.2 % | 3.2 % | ISO 527 | |
| Tensile Modulus | 7.30 GPa | 1060 ksi | 50 mm/min; ASTM D638 |
| 7.60 GPa | 1100 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 139 MPa | 20200 psi | ASTM D790 |
| 159 MPa | 23100 psi | ISO 178 | |
| Flexural Modulus | 6.20 GPa | 899 ksi | ASTM D790 |
| 8.70 GPa | 1260 ksi | ISO 178 | |
| Izod Impact, Notched | 1.17 J/cm | 2.19 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.04 J/cm | 13.2 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² | 21.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 3.00 J | 2.21 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 26.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
14.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 26.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
14.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 59.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 59.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C @Thickness 3.20 mm |
320 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 152 °C | 306 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 150 °C @Thickness 3.20 mm |
302 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® C7122 PC+ABS (Asia Pacific)
- Huntsman HY 825 US Polyamide
- Multibase Multi-Flex® D 4201 TPE Thermoplastic Elastomer
- LATI Larpeek 10 G/30 PEEK, 30% Glass Fiber Reinforced
- A. Schulman LP390-01 Narrow Molecular Weight Copolymer
- Domo 2340RC Polypropylene Copolymer
- AK Steel ASTM A 607 Class 2 Formable, Grade 45K Hot Rolled Carbon Steel, Medium/High Strength Low Alloy (HSLA)
- DuPont™ Surlyn® 1707 Sodium Ionomer
Copyright © lookpolymers.com All Rights Reserved