SABIC Innovative Plastics LNP THERMOCOMP MB006S PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP MB006S PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* MB006S is a compound based on Polypropylene resin containing 30% Glass Bead. Added features of this material include: Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in³ | ISO 1183 |
| 1.12 g/cc | 0.0405 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.0200 % | 0.0200 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0116 cm/cm @Time 86400 sec |
0.0116 in/in @Time 24.0 hour |
ISO 294 |
| 0.012 cm/cm @Time 86400 sec |
0.012 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm @Time 86400 sec |
0.011 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0115 cm/cm @Time 86400 sec |
0.0115 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ASTM D638 |
| 19.0 MPa | 2760 psi | ISO 527 | |
| Tensile Strength, Yield | 24.0 MPa | 3480 psi | ASTM D638 |
| 24.0 MPa | 3480 psi | ISO 527 | |
| Elongation at Break | 83.4 % | 83.4 % | ISO 527 |
| 87.5 % | 87.5 % | ASTM D638 | |
| Elongation at Yield | 5.5 % | 5.5 % | ISO 527 |
| 6.3 % | 6.3 % | ASTM D638 | |
| Tensile Modulus | 2.40 GPa | 348 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 44.0 MPa | 6380 psi | ASTM D790 |
| 46.0 MPa | 6670 psi | ISO 178 | |
| Flexural Modulus | 2.13 GPa | 309 ksi | ASTM D790 |
| 2.90 GPa | 421 ksi | ISO 178 | |
| Izod Impact, Notched | 0.210 J/cm | 0.393 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.34 J/cm | 4.38 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² | 0.952 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 3.00 J | 2.21 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 68.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 68.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C @Thickness 3.20 mm |
234 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 70.0 °C @Thickness 3.20 mm |
158 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nylene® 9533 , 33% Glass Reinforced Nylon 6/12
- Nilit Nilamon A3 H K8 40% Mineral Reinforced PA66
- SABIC Innovative Plastics Lexan® 943A PC (Asia Pacific)
- Indium Corp. Indalloy 79 Bismuth-Lead-Tin Solder Alloy
- Global PC/ABS-1218 Standard PC/ABS Grade
- Plenco 2369 Phenolic, Granular, Transfer Molded
- ChevronTexaco A-50 Jet Fuel
- Akro-Plastic Akromid® B3 GF 60 (2476) PA 6 Dry, 60% Glass Filled
- Zhejiang Juner PC-A1-9A Top-Grade Flame Retardant UV-Resistant
- Polyram RamTough PZ715 Polycarbonate, UV Stabilized
Copyright © lookpolymers.com All Rights Reserved