SABIC Innovative Plastics LNP THERMOCOMP LX08411 PEEK
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP LX08411 PEEK.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* LX08411 is a compound based on Polyetheretherketone resin containing Carbon Fiber. Added feature of this material is: Opaque.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0300 % | 0.0300 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0028 cm/cm @Time 86400 sec |
0.0020 - 0.0028 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0075 - 0.0085 cm/cm @Time 86400 sec |
0.0075 - 0.0085 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 270 MPa | 39200 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 270 MPa | 39200 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 1.8 % | 1.8 % | Type I, 5 mm/min; ASTM D638 |
| Elongation at Yield | 1.8 % | 1.8 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 23.51 GPa | 3410 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 366 MPa | 53100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 366 MPa | 53100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 25.0 GPa | 3630 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.700 J/cm | 1.31 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.75 J/cm | 14.5 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 341 °C @Thickness 3.20 mm |
646 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 327 °C @Thickness 3.20 mm |
621 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Omni Plastics OmniTuff™ HPP GRC40 Homopolymer Polypropylene Glass Reinforced
- Renegade Materials Corporation MVK-14 Polyimide FreeForm™ Astroquartz 4581 Fabric
- Hyosung Topilene F301U PP
- Hong Kun Group Aloe-Emodin Pharmaceutical Intermediate
- A. Schulman LP552-01 Narrow Molecular Weight Copolymer, High-Density Polyethylene
- Westlake Plastics PES film Made from ULTRASON® E Polyethersulfone Resin
- Chesterton ARC 988 Composite
- Cytec Thornel® T-605/50X 12K Carbon Fiber, Polyacrylonitrile (PAN) Precursor
Copyright © lookpolymers.com All Rights Reserved