DuPont Performance Polymers Delrin® FG100P NC010 Acetal (POM)  (Unverified Data**)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced
Manufacturer DuPont Performance Polymers
Trade Name Delrin®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Delrin® FG100P NC010 Acetal (POM)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High Viscosity Acetal Homopolymer Developed for Food Contact Applications Delrin FG100P is a high viscosity acetal homopolymer with improved thermal stability for use in easy to fill molds. It has been developed for consideration into applications suchInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
ISO 1183
Water Absorption 1.4 %

@Thickness 2.00 mm
 1.4 %

@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.300 %

@Thickness 2.00 mm
 0.300 %

@Thickness 0.0787 in
 Sim. to ISO 62
Viscosity 138000 cP

@Shear Rate 5000 1/s,
Temperature 230 °C
 138000 cP

@Shear Rate 5000 1/s,
Temperature 446 °F
 ISO 11403-1 -2
153500 cP

@Shear Rate 5000 1/s,
Temperature 215 °C
 153500 cP

@Shear Rate 5000 1/s,
Temperature 419 °F
 ISO 11403-1 -2
170500 cP

@Shear Rate 5000 1/s,
Temperature 200 °C
 170500 cP

@Shear Rate 5000 1/s,
Temperature 392 °F
 ISO 11403-1 -2
702600 cP

@Shear Rate 500 1/s,
Temperature 230 °C
 702600 cP

@Shear Rate 500 1/s,
Temperature 446 °F
 ISO 11403-1 -2
762300 cP

@Shear Rate 500 1/s,
Temperature 215 °C
 762300 cP

@Shear Rate 500 1/s,
Temperature 419 °F
 ISO 11403-1 -2
814100 cP

@Shear Rate 500 1/s,
Temperature 200 °C
 814100 cP

@Shear Rate 500 1/s,
Temperature 392 °F
 ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.022 cm/cm
0.022 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.020 cm/cm
0.020 in/in
ISO 294-4 2577
Melt Flow 1.9 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 1.9 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 cm³/10min; ISO 1133
2.5 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 2.5 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell M 92
92
ISO 2039-2
Hardness, Rockwell R 120
120
ISO 2039-2
Tensile Stress 10.8 MPa

@Strain 1.10 %,
Temperature 90.0 °C
 1570 psi

@Strain 1.10 %,
Temperature 194 °F
 ISO 11403-1 -2
27.2 MPa

@Strain 4.40 %,
Temperature 90.0 °C
 3950 psi

@Strain 4.40 %,
Temperature 194 °F
 ISO 11403-1 -2
32.4 MPa

@Strain 7.60 %,
Temperature 90.0 °C
 4700 psi

@Strain 7.60 %,
Temperature 194 °F
 ISO 11403-1 -2
33.6 MPa

@Strain 10.9 %,
Temperature 90.0 °C
 4870 psi

@Strain 10.9 %,
Temperature 194 °F
 ISO 11403-1 -2
35.5 MPa

@Strain 2.00 %,
Temperature 40.0 °C
 5150 psi

@Strain 2.00 %,
Temperature 104 °F
 ISO 11403-1 -2
42.0 MPa

@Strain 2.40 %,
Temperature 23.0 °C
 6090 psi

@Strain 2.40 %,
Temperature 73.4 °F
 ISO 11403-1 -2
52.0 MPa

@Strain 2.40 %,
Temperature 0.000 °C
 7540 psi

@Strain 2.40 %,
Temperature 32.0 °F
 ISO 11403-1 -2
57.0 MPa

@Strain 8.00 %,
Temperature 40.0 °C
 8270 psi

@Strain 8.00 %,
Temperature 104 °F
 ISO 11403-1 -2
57.7 MPa

@Strain 2.30 %,
Temperature -20.0 °C
 8370 psi

@Strain 2.30 %,
Temperature -4.00 °F
 ISO 11403-1 -2
59.5 MPa

@Strain 14.0 %,
Temperature 40.0 °C
 8630 psi

@Strain 14.0 %,
Temperature 104 °F
 ISO 11403-1 -2
62.1 MPa

@Strain 2.10 %,
Temperature -40.0 °C
 9010 psi

@Strain 2.10 %,
Temperature -40.0 °F
 ISO 11403-1 -2
63.6 MPa

@Strain 9.80 %,
Temperature 23.0 °C
 9220 psi

@Strain 9.80 %,
Temperature 73.4 °F
 ISO 11403-1 -2
65.5 MPa

@Strain 17.1 %,
Temperature 23.0 °C
 9500 psi

@Strain 17.1 %,
Temperature 73.4 °F
 ISO 11403-1 -2
73.73 MPa

@Strain 9.60 %,
Temperature 0.000 °C
 10690 psi

@Strain 9.60 %,
Temperature 32.0 °F
 ISO 11403-1 -2
76.54 MPa

@Strain 21.59 %,
Temperature 0.000 °C
 11100 psi

@Strain 21.59 %,
Temperature 32.0 °F
 ISO 11403-1 -2
80.2 MPa

@Strain 9.20 %,
Temperature -20.0 °C
 11600 psi

@Strain 9.20 %,
Temperature -4.00 °F
 ISO 11403-1 -2
82.8 MPa

@Strain 16.1 %,
Temperature -20.0 °C
 12000 psi

@Strain 16.1 %,
Temperature -4.00 °F
 ISO 11403-1 -2
92.8 MPa

@Strain 13.0 %,
Temperature -40.0 °C
 13500 psi

@Strain 13.0 %,
Temperature -40.0 °F
 ISO 11403-1 -2
95.5 MPa

@Strain 22.7 %,
Temperature -40.0 °C
 13900 psi

@Strain 22.7 %,
Temperature -40.0 °F
 ISO 11403-1 -2
Tensile Strength, Yield 70.0 MPa
10200 psi
ISO 527-1/-2
Elongation at Break 45 %
45 %
Nominal; ISO 527-1/-2
Elongation at Yield 25 %
25 %
ISO 527-1/-2
Tensile Modulus 2.90 GPa
421 ksi
ISO 527-1/-2
Flexural Strength 74.0 MPa

@Strain 3.50 %
 10700 psi

@Strain 3.50 %
 ISO 178
Flexural Modulus 2.60 GPa
377 ksi
ISO 178
Shear Modulus 0.297 GPa

@Temperature 120 °C
 43.1 ksi

@Temperature 248 °F
 Dynamic; ISO 11403-1 -2
0.6221 GPa

@Temperature 60.0 °C
 90.23 ksi

@Temperature 140 °F
 Dynamic; ISO 11403-1 -2
0.8835 GPa

@Temperature 10.0 °C
 128.1 ksi

@Temperature 50.0 °F
 Dynamic; ISO 11403-1 -2
1.0443 GPa

@Temperature -30.0 °C
 151.47 ksi

@Temperature -22.0 °F
 Dynamic; ISO 11403-1 -2
1.4976 GPa

@Temperature -60.0 °C
 217.21 ksi

@Temperature -76.0 °F
 Dynamic; ISO 11403-1 -2
Secant Modulus 0.337 GPa

@Strain 19.5 %,
Temperature 23.0 °C
 48.9 ksi

@Strain 19.5 %,
Temperature 73.4 °F
 ISO 11403-1 -2
0.357 GPa

@Strain 7.00 %,
Temperature 100 °C
 51.8 ksi

@Strain 7.00 %,
Temperature 212 °F
 ISO 11403-1 -2
0.369 GPa

@Strain 9.90 %,
Temperature 80.0 °C
 53.5 ksi

@Strain 9.90 %,
Temperature 176 °F
 ISO 11403-1 -2
0.371 GPa

@Strain 25.9 %,
Temperature -40.0 °C
 53.9 ksi

@Strain 25.9 %,
Temperature -40.0 °F
 ISO 11403-1 -2
0.37375 GPa

@Strain 16.0 %,
Temperature 40.0 °C
 54.209 ksi

@Strain 16.0 %,
Temperature 104 °F
 ISO 11403-1 -2
0.453 GPa

@Strain 18.4 %,
Temperature -20.0 °C
 65.7 ksi

@Strain 18.4 %,
Temperature -4.00 °F
 ISO 11403-1 -2
0.512 GPa

@Strain 4.20 %,
Temperature 100 °C
 74.2 ksi

@Strain 4.20 %,
Temperature 212 °F
 ISO 11403-1 -2
0.624 GPa

@Strain 5.00 %,
Temperature 80.0 °C
 90.5 ksi

@Strain 5.00 %,
Temperature 176 °F
 ISO 11403-1 -2
0.64898 GPa

@Strain 9.80 %,
Temperature 23.0 °C
 94.128 ksi

@Strain 9.80 %,
Temperature 73.4 °F
 ISO 11403-1 -2
0.681 GPa

@Strain 2.10 %,
Temperature 100 °C
 98.8 ksi

@Strain 2.10 %,
Temperature 212 °F
 ISO 11403-1 -2
0.7125 GPa

@Strain 8.00 %,
Temperature 40.0 °C
 103.3 ksi

@Strain 8.00 %,
Temperature 104 °F
 ISO 11403-1 -2
0.714 GPa

@Strain 13.0 %,
Temperature -40.0 °C
 104 ksi

@Strain 13.0 %,
Temperature -40.0 °F
 ISO 11403-1 -2
0.768 GPa

@Strain 9.60 %,
Temperature 0.000 °C
 111 ksi

@Strain 9.60 %,
Temperature 32.0 °F
 ISO 11403-1 -2
0.840 GPa

@Strain 0.500 %,
Temperature 100 °C
 122 ksi

@Strain 0.500 %,
Temperature 212 °F
 ISO 11403-1 -2
0.872 GPa

@Strain 9.20 %,
Temperature -20.0 °C
 126 ksi

@Strain 9.20 %,
Temperature -4.00 °F
 ISO 11403-1 -2
0.975 GPa

@Strain 1.20 %,
Temperature 80.0 °C
 141 ksi

@Strain 1.20 %,
Temperature 176 °F
 ISO 11403-1 -2
1.75 GPa

@Strain 2.40 %,
Temperature 23.0 °C
 254 ksi

@Strain 2.40 %,
Temperature 73.4 °F
 ISO 11403-1 -2
1.775 GPa

@Strain 2.00 %,
Temperature 40.0 °C
 257.4 ksi

@Strain 2.00 %,
Temperature 104 °F
 ISO 11403-1 -2
2.17 GPa

@Strain 2.40 %,
Temperature 0.000 °C
 314 ksi

@Strain 2.40 %,
Temperature 32.0 °F
 ISO 11403-1 -2
2.5087 GPa

@Strain 2.30 %,
Temperature -20.0 °C
 363.86 ksi

@Strain 2.30 %,
Temperature -4.00 °F
 ISO 11403-1 -2
2.96 GPa

@Strain 2.10 %,
Temperature -40.0 °C
 429 ksi

@Strain 2.10 %,
Temperature -40.0 °F
 ISO 11403-1 -2