SABIC Innovative Plastics LNP THERMOCOMP KZ004 Acetal Copolymer
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, 20% Glass Fiber Reinforced |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP KZ004 Acetal Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* KZ004 is a compound based on Acetal Copolymer resin containing 20% Milled Glass.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.53 g/cc | 0.0553 lb/in³ | ASTM D792 |
| 1.53 g/cc | 0.0553 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.200 % | 0.200 % | 50% RH, 24 hrs; ASTM D570 |
| 0.340 % | 0.340 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.027 - 0.030 cm/cm @Time 86400 sec |
0.027 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| 0.027 - 0.030 cm/cm @Time 86400 sec |
0.027 - 0.030 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.018 - 0.020 cm/cm @Time 86400 sec |
0.018 - 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| 0.018 - 0.020 cm/cm @Time 86400 sec |
0.018 - 0.020 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 42.0 MPa | 6090 psi | ASTM D638 |
| 44.0 MPa | 6380 psi | ISO 527 | |
| Tensile Strength, Yield | 42.0 MPa | 6090 psi | ASTM D638 |
| 44.0 MPa | 6380 psi | ISO 527 | |
| Elongation at Break | 9.7 % | 9.7 % | ISO 527 |
| 22.9 % | 22.9 % | ASTM D638 | |
| Elongation at Yield | 7.1 % | 7.1 % | ISO 527 |
| 8.1 % | 8.1 % | ASTM D638 | |
| Tensile Modulus | 3.43 GPa | 497 ksi | 1 mm/min; ISO 527 |
| 3.96 GPa | 574 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 70.0 MPa | 10200 psi | ISO 178 |
| 75.0 MPa | 10900 psi | ASTM D790 | |
| Flexural Modulus | 3.31 GPa | 480 ksi | ISO 178 |
| 3.51 GPa | 509 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.39 J/cm | 10.1 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 37.0 kJ/m² | 17.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 2.00 J | 1.48 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 73.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
41.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 75.1 µm/m-°C @Temperature -40.0 - 40.0 °C |
41.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 79.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 80.1 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.5 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 106 °C | 223 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 91.0 °C @Thickness 3.20 mm |
196 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Northstar Polymers MPP-A50A High Performance Polyether
- Indium Corp. 1081 Wave Solder Flux, Water-Soluble
- GRECO ISOTHANE 5090A Polyether TPU Resin
- Lord Adhesives Metech 3501 Palladium Silver Conductor Composition
- Karina 42/165-RG-GE (CS) Red Color Concentrate for PVC
- Sylvin Technologies 8940-65 Natural PVC Extrusion Compound
- SABIC Innovative Plastics LNP STAT-LOY A3000T ABS (Europe-Africa-Middle East)
- Sichuan Deyang Haton® hGR31M1 Polyphenylene Sulfide
- UBE UPIMOL® SA201 Heat-Resistant Polyimide Shape
Copyright © lookpolymers.com All Rights Reserved