SABIC Innovative Plastics LNP THERMOCOMP JF006LXZ PES (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyethersulfone (PES) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP JF006LXZ PES (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* JF006LXZ is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: Low Extractible.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in³ | ISO 1183 |
| 1.61 g/cc | 0.0582 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.300 % | 0.300 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0025 cm/cm @Time 86400 sec |
0.0025 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0069 cm/cm @Time 86400 sec |
0.0069 in/in @Time 24.0 hour |
ISO 294 |
| 0.0070 cm/cm @Time 86400 sec |
0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 99.0 MPa | 14400 psi | ISO 527 |
| 113 MPa | 16400 psi | ASTM D638 | |
| Elongation at Break | 1.4 % | 1.4 % | ISO 527 |
| 1.8 % | 1.8 % | ASTM D638 | |
| Tensile Modulus | 9.79 GPa | 1420 ksi | 50 mm/min; ASTM D638 |
| 10.19 GPa | 1478 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 172 MPa | 24900 psi | ASTM D790 |
| 222 MPa | 32200 psi | ISO 178 | |
| Flexural Modulus | 9.23 GPa | 1340 ksi | ASTM D790 |
| 9.24 GPa | 1340 ksi | ISO 178 | |
| Izod Impact, Notched | 0.580 J/cm | 1.09 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.27 J/cm | 8.00 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 29.0 kJ/m² | 13.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 13.0 J | 9.59 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.1 µm/m-°C @Temperature -40.0 - 40.0 °C |
16.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 30.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
17.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 36.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
20.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 36.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
20.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 217 °C @Thickness 3.20 mm |
423 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 212 °C @Thickness 3.20 mm |
414 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Polimeri Europa Dutral® OCP 5050 (CS 2404) Ethylene - Propylene
- Rogers Corporation XT/duroid™ 8000 Thermoplastic Laminate, Circuit Material
- Parker Chomerics Tecknit Teckfip™ FIP-X Formed in Place Conductive Elastomer
- Huntsman HY 9130 Polyamide
- Styrolution Luran® S 778 T ASA
- Shin-Etsu Silicones LIMSâ„¢ KE2090-40AB Elastomer
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with TCP Plasticizer
- 3M Scotchcal™ 50-88 Graphic Film
- BASF Elastollan C 75 A TPUR
- Lehmann & Voss LUVOCOM® 1105-7173/BL PEEK, with glass fiber
Copyright © lookpolymers.com All Rights Reserved