SABIC Innovative Plastics LNP THERMOCOMP IF007 PA6.12
| Category | Polymer , Thermoplastic , Nylon , Nylon 612 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP IF007 PA6.12.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* IF007 is a compound based on Nylon 6/12 resin containing 35% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 150 MPa | 21800 psi | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 8.89 GPa | 1290 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 227 MPa | 32900 psi | ASTM D790 |
| Flexural Modulus | 8.27 GPa | 1200 ksi | ASTM D790 |
| Izod Impact, Notched | 0.850 J/cm | 1.59 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.01 J/cm | 15.0 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 198 °C @Thickness 3.20 mm |
388 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nyco NYAD® G Special Wollastonite
- SABIC Innovative Plastics Lexan® EXL1463T PC Copolymer (Asia Pacific)
- Kureha KF Polymer 850 PVDF Homopolymer
- A. Schulman POLYBATCH™ Silver 7002/5 Concentrate Based In LDPE
- ExxonMobil Bicor™ 19MB440 OPP Film
- Entec Hypro™ PPH-GF10 Natural Homopolymer Polypropylene, 10% Glass Reinforced
- Beijing Ranger Chem SM-603R Solid Epoxy Resin
Copyright © lookpolymers.com All Rights Reserved