SABIC Innovative Plastics LNP THERMOCOMP EF006E PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP EF006E PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* EF006E is a compound based on Polyetherimide resin containing 30% Glass Fiber. Added features of this material include: Easy Molding.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.53 g/cc | 0.0553 lb/in³ | ASTM D792 |
| 1.53 g/cc | 0.0553 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 169 MPa | 24500 psi | 5 mm/min; ISO 527 |
| 174 MPa | 25200 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.0 % | 2.0 % | 5 mm/min; ISO 527 |
| 2.1 % | 2.1 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 10.96 GPa | 1590 ksi | 1 mm/min; ISO 527 |
| 11.54 GPa | 1674 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 228 MPa | 33100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 231 MPa | 33500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 10.16 GPa | 1474 ksi | 2 mm/min; ISO 178 |
| 10.6 GPa | 1540 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.680 J/cm | 1.27 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.30 J/cm | 9.93 ft-lb/in | ASTM D4812 |
| Dart Drop, Total Energy | 13.0 J @Temperature 23.0 °C |
9.59 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 29.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
16.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 31.9 µm/m-°C @Temperature -30.0 - 30.0 °C |
17.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 208 °C | 406 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 207 °C @Thickness 3.20 mm |
405 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 203 °C | 397 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 203 °C @Thickness 3.20 mm |
397 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- ND Industries SuperGlue Ethyl 325
- LyondellBasell Hifaxâ„¢ CB229 Thermoplastic Olefin Resin
- Sylvin Technologies 8950-75 Natural PVC Extrusion Compound
- Shin-Etsu Silicones 541 Fluid
- Polyram PlusTek PA301G6 Nylon 6.6, Heat Stabilized, 30% Glass Fiber
- Wellman Wellamid® GSF25/15-66 22L-NBK1 40% Glass Sphere/Fiber Reinforced Nylon 66
- Wellman Wellamid® MRGST1715-WBK1 Nylon 6, 25% Mineral and Glass Sphere Reinforced, Impact Modified, Weatherable Grade
- Trelleborg Emerson & Cuming Eccobond® 1309 General Purpose Catalyst
- Colorite Polymers 3879 General Purpose Vinyl Compound
- Addiplast Addilene J 326 V30 Polypropylene Copolymer
Copyright © lookpolymers.com All Rights Reserved