Arkema Group Rilsan® AZM 23 T6LD Nylon 12, 23% Glass Fiber Filled (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 12 , Nylon 12, 20% Glass Fiber Filled
Manufacturer Arkema
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Rilsan® AZM 23 T6LD Nylon 12, 23% Glass Fiber Filled (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Designation ISO 1874-PA12,MHLR,16-050,GF23Rigid grade with glass fiber filler (23%) for injection molding. Available colors: black and natural. Reinforced light and heat stabilizing agent. Mold-release agent.Rigidity. High compressive strength. Very low shrinkage: include 0,5% on average for the design of the mold. Low coefficient of linear expansion. High dimensional stability.Example applications: Rigid mechanical parts.ISO data provided by the manufacturer, Arkema.
Physical Properties Metric English Comments
Melt Flow 3.2 g/10 min

@Load 2.16 kg,
Temperature 235 °C
3.2 g/10 min

@Load 4.76 lb,
Temperature 455 °F
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 82.0 MPa
11900 psi
5 mm/min
Elongation at Break 6.0 %
6.0 %
5 mm/min
Tensile Modulus 5.52 GPa
801 ksi
1 mm/min
Charpy Impact Unnotched 6.81 J/cm²
32.4 ft-lb/in²
6.28 J/cm²

@Temperature -30.0 °C
29.9 ft-lb/in²

@Temperature -22.0 °F
Charpy Impact, Notched 1.37 J/cm²
6.52 ft-lb/in²
0.810 J/cm²

@Temperature -30.0 °C
3.85 ft-lb/in²

@Temperature -22.0 °F
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 60.0 µm/m-°C

@Temperature 20.0 °C
33.3 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi) 173 °C
343 °F
Deflection Temperature at 1.8 MPa (264 psi) 165 °C
329 °F
Vicat Softening Point 165 °C
329 °F
50°C/hr; 50N