SABIC Innovative Plastics LNP THERMOCOMP DF008ERH PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP DF008ERH PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* DF008ERH is a compound based on Polycarbonate resin containing 40% Glass Fiber. Added features of this material include: Easy Molding, Mold Release, Healthcare.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Moisture Absorption | 0.120 % | 0.120 % | 23°C / 50% RH; ISO 62 |
| 0.930 % | 0.930 % | 50% RH, 24 hrs; ASTM D570 | |
| Linear Mold Shrinkage, Flow | 0.0016 cm/cm @Time 86400 sec |
0.0016 in/in @Time 24.0 hour |
ISO 294 |
| 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0035 cm/cm @Time 86400 sec |
0.0035 in/in @Time 24.0 hour |
ISO 294 |
| 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 136 MPa | 19700 psi | ASTM D638 |
| 136 MPa | 19700 psi | ISO 527 | |
| Elongation at Break | 2.2 % | 2.2 % | ISO 527 |
| 2.3 % | 2.3 % | ASTM D638 | |
| Tensile Modulus | 11.17 GPa | 1620 ksi | 1 mm/min; ISO 527 |
| 11.81 GPa | 1713 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 203 MPa | 29400 psi | ISO 178 |
| 204 MPa | 29600 psi | ASTM D790 | |
| Flexural Modulus | 10.97 GPa | 1591 ksi | ISO 178 |
| 11.26 GPa | 1633 ksi | ASTM D790 | |
| Izod Impact, Notched | 2.18 J/cm | 4.08 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.06 J/cm | 15.1 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 53.0 kJ/m² | 25.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 13.0 J | 9.59 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 32.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
18.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 32.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
18.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 35.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
19.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 35.1 µm/m-°C @Temperature -40.0 - 40.0 °C |
19.5 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 137 °C | 279 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 136 °C @Thickness 3.20 mm |
277 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- 3M Dyneon™ Fluorel™ FC-2174 Fluoroelastomer VF2 + HFP Dipolymer (discontinued **)
- Lord Adhesives Circalokâ„¢ EP-937 Epoxy Board Level Encapsulant
- SABIC Innovative Plastics SABIC PPCOMPOUND 19T1020 PP
- Schott S8809 Contrast Enhancement Filter
- A. Schulman PP 1692 Polypropylene High Impact Copolymer
- A. Schulman FORMION™ FI 372 Ionomer
- DuPont™ Kapton® 100EN Polyimide Film, 25 Micron Thickness
- Chosun Refractories ASM-34 Air-Setting Mortar
- China Tungsten Z20 Tungsten Carbide for Mining Purposes
- Adell BR-37 Nylon 6, 35% Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved