SABIC Innovative Plastics LNP THERMOCOMP DF004RXP PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP DF004RXP PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermocomp* DF004RXP is a compound based on Polycarbonate resin containing 20% Glass Fiber. Some light color grades may have lower impact data than natural and black. Added features include: Mold Release, UL
Physical Properties Metric English Comments
Density 1.35 g/cc
0.0488 lb/in³
ISO 1183
1.352 g/cc
0.04884 lb/in³
ASTM D792
Water Absorption 0.17 %

@Time 86400 sec
0.17 %

@Time 24.0 hour
ISO 62-1
Moisture Absorption 0.130 %
0.130 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0020 - 0.0040 cm/cm

@Time 86400 sec
0.0020 - 0.0040 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.0060 - 0.0080 cm/cm

@Time 86400 sec
0.0060 - 0.0080 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 102 MPa
14800 psi
Type I, 5 mm/min; ASTM D638
103 MPa
14900 psi
5 mm/min; ISO 527
Tensile Strength, Yield 105 MPa
15200 psi
Type I, 5 mm/min; ASTM D638
105 MPa
15200 psi
5 mm/min; ISO 527
Elongation at Break 3.2 %
3.2 %
Type I, 5 mm/min; ASTM D638
3.3 %
3.3 %
5 mm/min; ISO 527
3.7 %
3.7 %
Flexural Strain, break, 2 mm/min; ISO 178
Elongation at Yield 2.9 %
2.9 %
Type I, 5 mm/min; ASTM D638
3.0 %
3.0 %
5 mm/min; ISO 527
Tensile Modulus 5.72 GPa
830 ksi
1 mm/min; ISO 527
6.10 GPa
885 ksi
50 mm/min; ASTM D638
Flexural Strength 163 MPa
23600 psi
2 mm/min; ISO 178
169 MPa
24500 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Yield Strength 163 MPa
23600 psi
2 mm/min; ISO 178
173 MPa
25100 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 5.88 GPa
853 ksi
2 mm/min; ISO 178
6.07 GPa
880 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.980 J/cm
1.84 ft-lb/in
Light & White Colors; ASTM D256
1.25 J/cm
2.34 ft-lb/in
ASTM D256
1.25 J/cm
2.34 ft-lb/in
Natural & Black Colors; ASTM D256
Izod Impact, Unnotched 8.95 J/cm
16.8 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 12.0 kJ/m²
5.71 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 53.0 kJ/m²
25.2 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 24.0 J
17.7 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 5.00 J
3.69 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 28.9 µm/m-°C

@Temperature -30.0 - 30.0 °C
16.1 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
CTE, linear, Transverse to Flow 53.9 µm/m-°C

@Temperature -30.0 - 30.0 °C
29.9 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
Deflection Temperature at 1.8 MPa (264 psi) 140 °C
284 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
141 °C

@Thickness 3.20 mm
286 °F

@Thickness 0.126 in
unannealed; ASTM D648
Flammability, UL94 HB

@Thickness 0.750 - 3.00 mm
HB

@Thickness 0.0295 - 0.118 in
UL 94