- PolyOne Geon™ Vinyl Dry Blend E6755 Polyvinyl Chloride, Rigid (PVC, Rigid)
PolyOne Geon™ Vinyl Dry Blend E6755 Polyvinyl Chloride, Rigid (PVC, Rigid)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ Vinyl Dry Blend E6755 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ASTM D1638 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 82 | 82 | ASTM D2240 |
| Tensile Strength, Yield | 45.1 MPa | 6540 psi | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 2.76 GPa | 400 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 82.0 MPa | 11900 psi | ASTM D790 |
| Flexural Modulus | 2.81 GPa | 408 ksi | ASTM D790 |
| Izod Impact, Notched | 11.0 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
20.6 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded; ASTM D256A |
| Dart Drop Total Energy | 55.2 J/cm @Temperature 23.0 °C |
0.103 ft-lb/mil @Temperature 73.4 °F |
Procedure A, C.125; ASTM D4226 |
| 245 J/cm @Temperature 23.0 °C |
0.459 ft-lb/mil @Temperature 73.4 °F |
Procedure B, C.125; ASTM D4226 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 65.0 µm/m-°C | 36.1 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 69.0 °C @Thickness 3.18 mm |
156 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 193 - 210 °C | 379 - 410 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Good Thermal Stability | |
| High Impact Resistance | ||
| Forms | Powder | |
| Generic Material | PVC, Rigid | |
| Generic Name | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
| Processing Method | Extrusion | |
| Profile Extrusion | ||
| PVC Cell Classification | 16353 | ASTM D1784 |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Automotive Interior Parts | |
| Fencing & Decking | ||
| Profiles | ||
| Sheet |
Users viewing this material also viewed the following:
- NOVA Chemicals EPS M97C Expandable Polystyrene Resin
- Indium Corp. Indalloy 154 Tin-Lead Solder Alloy
- Materion Beryllium Copper Alloy 3 Forgings & Extrusions; A (TB00) Temper (UNS C17510)
- Indium Corp. Indalloy 88 Indium Solder Alloy
- IRPC Polimaxx Polene R1760 High Density Polyethylene
- Lubriplate APG-140 Petroleum-Based Gear, Bearing, & Recirculating Oil
- A. Schulman POLYFORT™ FPP 1200 Calcium Carbonate-Filled Homopolymer Polypropylene
- ExxonMobil LD 317.09 Film Resin
- Eagle Brass 101 OFE COPPER (Certified), Extra Hard
- Eurostar Starflam AFR450B1 PA66, Glass Fiber Reinforced, Flame Retardant, Injection Molding
Copyright © lookpolymers.com All Rights Reserved