| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP DF004ER PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* DF004ER is a compound based on Polycarbonate resin containing 20% Glass Fiber. Added features of this material include: Easy Molding. Mold Release.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 |
| 1.322 g/cc | 0.04776 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.110 % | 0.110 % | 50% RH, 24 hrs; ASTM D570 |
| 0.170 % | 0.170 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0030 cm/cm @Time 86400 sec |
0.0020 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0020 - 0.0030 cm/cm @Time 86400 sec |
0.0020 - 0.0030 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0050 cm/cm @Time 86400 sec |
0.0040 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0043 - 0.0050 cm/cm @Time 86400 sec |
0.0043 - 0.0050 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 96.0 MPa | 13900 psi | ASTM D638 |
| 96.0 MPa | 13900 psi | ISO 527 | |
| Elongation at Break | 3.7 % | 3.7 % | ASTM D638 |
| 3.8 % | 3.8 % | ISO 527 | |
| Tensile Modulus | 5.62 GPa | 815 ksi | 1 mm/min; ISO 527 |
| 5.65 GPa | 819 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 166 MPa | 24100 psi | ASTM D790 |
| 166 MPa | 24100 psi | ISO 178 | |
| Flexural Modulus | 5.58 GPa | 809 ksi | ASTM D790 |
| 5.75 GPa | 834 ksi | ISO 178 | |
| Izod Impact, Notched | 1.44 J/cm | 2.70 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.54 J/cm | 16.0 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 53.0 kJ/m² | 25.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 16.0 J | 11.8 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 6.00 J | 4.43 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 41.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
23.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 41.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
23.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 53.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
29.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 53.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
29.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 286 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 140 °C @Thickness 3.20 mm |
284 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Eastman 5284 LDPE 8% EVA Copolymer, High Clarity, Ultra-High Impact Film Resin (discontinued **)
- KB Alloys 20% Calcium Aluminum Alloy
- Ineos ABS Triax® 3158 ABS + Polyamide Blend (DAM), PA66/ABS Pellets (filled)
- Ineos L06Z-00 Polypropylene Impact Copolymer
- Westlake Hifor Xtreme SC74842 Linear Low Density Polyethylene
- Dow Corning CE-8170 AF MICROEMULSION
- Epoxy Technology EPO-TEK® 302-3M Optically Transparent Epoxy
- Eurotec® Tecodur® PB70 GR15 BK002 XA21 PBT, 15% glass fiber reinforced, flame retardant - halogen (RoHS compliant), heat stabilized, natural
- BASF Styropor® F 415-N Expandable Polystyrene
- DuPont Performance Polymers Rynite® 545 NC010 PET (Unverified Data**)