SABIC Innovative Plastics LNP THERMOCOMP DF0029ER PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP DF0029ER PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* DF0029ER is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release, Flame Retardant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ASTM D792 |
| 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0067 cm/cm @Time 86400 sec |
0.0067 in/in @Time 24.0 hour |
ISO 294 |
| 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0068 cm/cm @Time 86400 sec |
0.0068 in/in @Time 24.0 hour |
ISO 294 |
| 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 79.0 MPa | 11500 psi | ASTM D638 |
| 81.0 MPa | 11700 psi | ISO 527 | |
| Tensile Strength, Yield | 83.0 MPa | 12000 psi | ASTM D638 |
| 84.0 MPa | 12200 psi | ISO 527 | |
| Elongation at Break | 4.7 % | 4.7 % | ISO 527 |
| 5.5 % | 5.5 % | ASTM D638 | |
| Elongation at Yield | 3.7 % | 3.7 % | ISO 527 |
| 3.9 % | 3.9 % | ASTM D638 | |
| Tensile Modulus | 4.13 GPa | 599 ksi | 50 mm/min; ASTM D638 |
| 4.46 GPa | 647 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 129 MPa | 18700 psi | ISO 178 |
| Flexural Modulus | 4.10 GPa | 595 ksi | ISO 178 |
| 4.13 GPa | 599 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.850 J/cm | 1.59 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.65 J/cm | 16.2 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 59.0 kJ/m² | 28.1 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 16.0 J | 11.8 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 7.00 J | 5.16 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 50.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
28.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 59.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
32.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 59.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 289 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 142 °C @Thickness 3.20 mm |
288 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 136 °C | 277 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- Formosa Plastics Formolene® L43840U Rotational Molding LLDPE (discontinued **)
- SABIC Innovative Plastics LNP LUBRICOMP DFI14 PC
- Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick
- Techmer ES HiFill® PA6 X BN071 EL MB Nylon 6
- Zylog Hipolyene® 1533 NM Thermoplastic Polyolefin & PP Compound
- Hexcel® Redux® 312L Modified epoxy film adhesive
- AK Steel 15-5 PH® Precipitation Hardening Stainless Steel, Condition H 1150-M
- BASF Capron® 8234G 44% Glass-Filled Nylon 6 (Dry) (discontinued **)
- Eurostar Staramide BG3ST42 PA6, Glass Fiber Filled, Impact Modified, Injection Molded
Copyright © lookpolymers.com All Rights Reserved