Dow Nordel® IP 4640 Molded Golf Grips
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | Dow Chemical |
| Trade Name | Nordel® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Dow Nordel® IP 4640 Molded Golf Grips.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
FormulationNordel® IP 4640
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.057 g/cc | 0.03819 lb/in³ | |
| Mooney Viscosity | 49 @Temperature 100 °C |
49 @Temperature 212 °F |
ML 1 + 4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 58 | 58 | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Elongation at Break | 657 % | 657 % | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 100% Modulus | 0.00170 GPa | 0.247 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 200% Modulus | 0.00260 GPa | 0.377 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 300% Modulus | 0.00370 GPa | 0.537 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tear Strength | 27.8 kN/m | 159 pli | Die C, Vulcanizate, Press cured, TC95 +3min at 160°C |
| Compression Set | 88 % @Temperature 125 °C |
88 % @Temperature 257 °F |
Pellets cured MDR TC95 + 15 min at 160°C, 70 hr at 125°C; Method B |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Brittleness Temperature | -41.0 °C | -41.8 °F | Temperature Retraction, TR-10 |
Users viewing this material also viewed the following:
- PolyOne Maxxam™ SY 89-22-7 Polypropylene, Unspecified (PP, Unspecified)
- NanoAmor 95%, OD: 30-50 nm COOH Functionalized Aligned Multi-Walled Carbon Nanotubes
- Pinnacle Polymers 3208 High Impact Polypropylene Copolymer, Injection Molding Grade
- LATI Latamid 6 E02 PA 6, Impact modified
- Karina E 6048/1-TRE Kariprene Black
- Solvay MACKANATE® OPSV Surfactant
- A. Schulman SCHULAMID® 6 GF50H 50% Glass Fiber Reinforced Nylon 6
- Dow Corning LSPBK 22 SILICONE MASTERBATCH
- H.C. Starck Amperit® 584.1 Chromium Carbide-Nickel Chromium 75-25 (Cr3C2-NiCr)
Copyright © lookpolymers.com All Rights Reserved