Chosun Refractories INCT-110S Light-Weight Castable
| Category | Ceramic |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chosun Refractories INCT-110S Light-Weight Castable.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 1.44e-7 - 0.000491 GPa @Temperature 110 °C, Time 86400 sec |
0.0000209 - 0.0711 ksi @Temperature 230 °F, Time 24.0 hour |
|
| 0.0004905 - 0.0014715 GPa @Temperature 500 °C, Time 10800 sec |
0.07114 - 0.21343 ksi @Temperature 932 °F, Time 3.00 hour |
||
| 0.0014715 - 0.0024525 GPa @Temperature 1000 °C, Time 10800 sec |
0.21343 - 0.35571 ksi @Temperature 1830 °F, Time 3.00 hour |
||
| Compressive Strength | 0.981 - 2.94 MPa @Temperature 500 °C, Time 10800 sec |
142 - 427 psi @Temperature 932 °F, Time 3.00 hour |
Cold Crushing Strength |
| 1.96 - 4.90 MPa @Temperature 1000 °C, Time 10800 sec |
284 - 711 psi @Temperature 1830 °F, Time 3.00 hour |
Cold Crushing Strength | |
| 1.96 - 4.90 MPa @Temperature 110 °C, Time 86400 sec |
284 - 711 psi @Temperature 230 °F, Time 24.0 hour |
Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.1628 W/m-K @Temperature 260 °C |
1.128 BTU-in/hr-ft²-°F @Temperature 500 °F |
|
| 0.1977 W/m-K @Temperature 540 °C |
1.370 BTU-in/hr-ft²-°F @Temperature 1000 °F |
||
| 0.2443 W/m-K @Temperature 800 °C |
1.692 BTU-in/hr-ft²-°F @Temperature 1470 °F |
||
| Maximum Service Temperature, Air | 1100 °C | 2010 °F | limited |
| Shrinkage | -0.800 % @Temperature 1000 °C, Time 10800 sec |
-0.800 % @Temperature 1830 °F, Time 3.00 hour |
|
| -0.0600 % @Temperature 110 °C, Time 86400 sec |
-0.0600 % @Temperature 230 °F, Time 24.0 hour |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 30 % | 30 % | |
| SiO2 | 37 % | 37 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Installation Method | Casting, Troweling | |
| Main Applications | General furnaces | |
| Material Required for Estimating (kg/?) | 800 | |
| Water Required for Casting(%) | 50-60 |
Users viewing this material also viewed the following:
- Premix Thermoplastics PRE-ELEC® PS 1328
- Polymer Resources PPX-GP3 Modified-PPO, General Purpose
- NOVA Chemicals Novapol® LM-1019-A LDPE Masterbatch Resin (discontinued **)
- Materion BrushCAST® 275C High Strength Casting Alloy (As Cast)
- Topas Advanced Polymers TOPAS® 8007X10 Cyclic Olefin Copolymer (COC)
- Cotronics Resbond™ 903HP High Temperature Ceramic Adhesive, Hi-Bond Strength
- Hippe MF CC 201 Woven Cotton Cloth Reinforced Melamine Resin - Sheet
- ExxonMobil Gargoyle Arctic 230 SHC 200 Series
- BNZ Materials BNZ-3000 Insulating Firebrick
Copyright © lookpolymers.com All Rights Reserved