SABIC Innovative Plastics LNP STAT-LOY SLDM2005 PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Stat-loy |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-LOY SLDM2005 PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Antistatic Polycarbonate, Non Halogen FR V-2 grade, mineral 5% filled
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Moisture Absorption | 0.0300 % | 0.0300 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.60 % | 0.60 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 17 g/10 min @Load 2.16 kg, Temperature 260 °C |
17 g/10 min @Load 4.76 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 46.0 MPa | 6670 psi | Type I, 5 mm/min; ASTM D638 |
| 46.0 MPa | 6670 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 53.0 MPa | 7690 psi | 5 mm/min; ISO 527 |
| 54.0 MPa | 7830 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 46 % | 46 % | 5 mm/min; ISO 527 |
| 72 % | 72 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 4.0 % | 4.0 % | Type I, 5 mm/min; ASTM D638 |
| 4.0 % | 4.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 2.60 GPa | 377 ksi | 1 mm/min; ISO 527 |
| 2.83 GPa | 410 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 84.0 MPa | 12200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 88.0 MPa | 12800 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 2.35 GPa | 341 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.63 GPa | 381 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 2.94 J/cm | 5.51 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C @Thickness 3.20 mm |
210 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Flammability, UL94 | V-2 @Thickness 2.00 mm |
V-2 @Thickness 0.0787 in |
UL 94 by SABIC-IP |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 5.00e+12 ohm | 5.00e+12 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Nilit FRIANYL B63 SG 10 Nylon 6 for injection molding, 10% mineral filled
- Ineos ABS Lustran® 556
- Lubriplate PURE TAC PURE Aluminum Complex USP Mineral Oil-Based Food Machinery Grade Grease
- SABIC Innovative Plastics ULTEM 2210R PEI
- A. Schulman SCHULAMID® 6 MV5 Unreinforced Nylon 6
- DuPont Teijin Films Mylar® EB11 Polyester Film, 48 Gauge
- Ascend Performance Materials Vydyne® 41H BK03 Nylon 66, Impact Modified, DAM
- Budd DSM-949, Diesel Grade SMC, Vinyl Ester, Black (discontinued **)
Copyright © lookpolymers.com All Rights Reserved