Chase Plastics CP Pryme® AC100-27 Acetal Copolymer Molding Resin

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer Chase Plastics
Trade Name CP Pryme®
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF Chase Plastics CP Pryme® AC100-27 Acetal Copolymer Molding Resin.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Information provided by Chase Plastics.
Physical Properties Metric English Comments
Specific Gravity 1.41 g/cc
1.41 g/cc
ASTM D792
Water Absorption 0.22 %
0.22 %
24 hours; ASTM D570
Melt Flow 27 g/10 min
<br>@Load 2.16 kg,<br> Temperature 190 °C
 27 g/10 min
<br>@Load 4.76 lb,<br> Temperature 374 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 62.7 MPa
9100 psi
ASTM D638
Elongation at Break 65 %
65 %
ASTM D638
Flexural Strength 90.3 MPa
13100 psi
ASTM D790
Flexural Modulus 2.60 GPa
377 ksi
ASTM D790
Izod Impact, Notched 0.587 J/cm
1.10 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 160 °C
<br>@Thickness 3.17 mm
 320 °F
<br>@Thickness 0.125 in
 Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 110 °C
<br>@Thickness 3.17 mm
 230 °F
<br>@Thickness 0.125 in
 Unannealed; ASTM D648