- SABIC Innovative Plastics LNP STAT-KON Noryl_HMC3008A PPE+HIPS (Europe-Africa-Middle East)
SABIC Innovative Plastics LNP STAT-KON Noryl_HMC3008A PPE+HIPS (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON Noryl_HMC3008A PPE+HIPS (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Stat-kon* Noryl_HMC3008A compound is a 30% glass/mineral/carbon fiber reinforced resin; static dissipative; 250F (120C) HDT. Tight tolerance molding.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.28 g/cc | 1.28 g/cc | ASTM D792 |
| Water Absorption | 0.060 % @Time 86400 sec |
0.060 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.00050 - 0.0015 cm/cm @Thickness 3.20 mm |
0.00050 - 0.0015 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0015 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0015 - 0.0030 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength at Break | 104 MPa | 15100 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 99.0 MPa | 14400 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | Type I, 5 mm/min; ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 127 MPa | 18400 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 9.85 GPa | 1430 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 1.49 J/cm | 2.79 ft-lb/in | ASTM D4812 |
| Taber Abrasion, mg/1000 Cycles | 77 | 77 | CS-17, 1 kg; ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 121 °C @Thickness 6.40 mm |
250 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| UL RTI, Electrical | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical with Impact | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical without Impact | 50.0 °C | 122 °F | UL 746B |
| Flammability, UL94 | V-1 @Thickness 2.48 mm |
V-1 @Thickness 0.0976 in |
UL 94 |
| Oxygen Index | 39 % | 39 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1000 ohm-cm | 1000 ohm-cm | ASTM D257 |
| Surface Resistance | 1e+05 | 1e+05 | ASTM D257 |
| Static Decay | 0.010 sec | 0.010 sec | 5000V to <50V; FTMS101B |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycolac® MG47 ABS (Europe-Africa-Middle East)
- Ravago Manufacturing Americas Hylon® N2015L Nylon 6 (Cond)
- SABIC Innovative Plastics LNP THERMOCOMP UF004AS PPA (Europe-Africa-Middle East)
- Total PPH 3847MR Polypropylene, Radiation Resistant - Clarified - High Flow for Injection Molding
- EPICHEM Epinyl PA 66 GF25 AU Polyamide 66, 25% Glass, Self extinguishing
- E-Polymers TEKAMID® TB120G60W , 62% Glass Fiber Reinforced PA6, DAM
- Asahi Kasei Leona® 13G43 43% Glass Filled Nylon 66
- SABIC Innovative Plastics LNP LUBRICOMP DBL349E PC (Asia Pacific)
- Karina E 08/415-FC-LMP Beige Color Concentrate for PVC
Copyright © lookpolymers.com All Rights Reserved