SABIC Innovative Plastics LNP STAT-KON Noryl_HMC1508 PPE+HIPS (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON Noryl_HMC1508 PPE+HIPS (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Stat-kon* Noryl_HMC1508 compound is a static dissipative NORYL resin.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0015 - 0.0025 cm/cm @Thickness 3.20 mm |
0.0015 - 0.0025 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0020 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0030 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | Type I, 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 131 MPa | 19000 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 7.00 GPa | 1020 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 121 °C @Thickness 6.40 mm |
250 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| UL RTI, Electrical | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical with Impact | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical without Impact | 50.0 °C | 122 °F | UL 746B |
| Flammability, UL94 | V-1 @Thickness 1.49 mm |
V-1 @Thickness 0.0587 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 20000 ohm-cm | 20000 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+6 ohm | 1.00e+6 ohm | ASTM D257 |
| Static Decay | 0.010 sec | 0.010 sec | 5000V to <50V; FTMS101B |
Users viewing this material also viewed the following:
- Northstar Polymers PNA-216 Curing Agent
- Kazanorgsintez 153-10K Polyethylene Composition for Cable Industry
- Gouda Vuurvast AK 60 C Dense Refractory Brick
- Toyobo Vylopet® EMC615 PET/PBT Blend
- A. Schulman POLYBLAK™ 3209 Superior Black Color Concentrate, 40% Carbon Black Based In Polypropylene
- Chesterton OPTICOOL™ 570 Lubrication
- Domo Domamid® 28 Polyamide 6
- Braskem LL6901S LLDPE Blown Film Extrusion Polyethylene Copolymer
- DuPont Performance Polymers Zytel® 79G13HSL BK039 Nylon 66 (Unverified Data**)
- Resinlab® EP11HT Gray Filled Epoxy Adhesive
Copyright © lookpolymers.com All Rights Reserved