SABIC Innovative Plastics LNP STAT-KON MFD03 PP (Asia Pacific)
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON MFD03 PP (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Stat-kon* MFD03 is a compound based on Polypropylene resin containing Glass Fiber, Carbon Powder. Added features of this material include: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ASTM D792 |
| 1.07 g/cc | 0.0387 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.010 cm/cm @Time 86400 sec |
0.010 in/in @Time 24.0 hour |
ASTM D955 |
| 0.010 cm/cm @Time 86400 sec |
0.010 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm @Time 86400 sec |
0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0092 cm/cm @Time 86400 sec |
0.0092 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 15.0 MPa | 2180 psi | ISO 527 |
| 16.0 MPa | 2320 psi | ASTM D638 | |
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM D638 |
| 34.0 MPa | 4930 psi | ISO 527 | |
| Elongation at Break | 5.7 % | 5.7 % | ISO 527 |
| 6.9 % | 6.9 % | ASTM D638 | |
| Elongation at Yield | 2.6 % | 2.6 % | ISO 527 |
| 2.7 % | 2.7 % | ASTM D638 | |
| Tensile Modulus | 3.31 GPa | 480 ksi | 1 mm/min; ISO 527 |
| 3.44 GPa | 499 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 51.0 MPa | 7400 psi | ISO 178 |
| Flexural Modulus | 2.75 GPa | 399 ksi | ASTM D790 |
| 3.00 GPa | 435 ksi | ISO 178 | |
| Izod Impact, Notched | 3.47 J/cm | 6.50 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 1.38 J/cm | 2.59 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 22.0 kJ/m² | 10.5 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 13.0 J | 9.59 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 5.00 J | 3.69 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 104 µm/m-°C @Temperature -40.0 - 40.0 °C |
57.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 105 µm/m-°C @Temperature -40.0 - 40.0 °C |
58.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 46.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
26.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 47.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
26.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C | 288 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 147 °C @Thickness 3.20 mm |
297 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 98.0 °C | 208 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 106 °C @Thickness 3.20 mm |
223 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Karina E 898-10/161-IS-RG White PVC Compound
- SABIC Innovative Plastics LNP LUBRICOMP RAL22 PA 66 (Europe-Africa-Middle East)
- Supreme Petrochem SP 6425 9885 Abrasion Resistant Polystyrene
- Voloknohim Nylon Fiber 0.68 tex
- Chengdu Polyster H4543B Thermoplastic Polyether-ester Elastomer (TPEE)
- Dow C719-35RNHP Polypropylene
- CP-Polymer-Technik Wellamid® 6000 GV 30 HWCP 30% Glass Fiber Nylon 6, Heat Stabilized, Dry
- AIM 58 Fusible Alloy
- A. Schulman POLYBATCH™ Green 300 Concentrate Based In Polyethylene
- PlastxWorld CEVIAN®-V 400N ABS
Copyright © lookpolymers.com All Rights Reserved