SABIC Innovative Plastics LNP STAT-KON MD000A PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON MD000A PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* MD000A is a compound based on Polypropylene resin containing Carbon. Added feature of this grade is: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.00 g/cc | 1.00 g/cc | ASTM D792 |
| Density | 0.998 g/cc | 0.0361 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 25.0 MPa | 3630 psi | 5 mm/min; ISO 527 |
| 26.0 MPa | 3770 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.8 % | 2.8 % | 5 mm/min; ISO 527 |
| 3.1 % | 3.1 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 1.77 GPa | 257 ksi | 1 mm/min; ISO 527 |
| 1.87 GPa | 271 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 40.0 MPa | 5800 psi | ISO 178 |
| Flexural Modulus | 1.65 GPa | 239 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 1.66 GPa | 241 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.450 J/cm | 0.843 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.29 J/cm | 15.5 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 48.0 kJ/m² | 22.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 26.0 J @Temperature 23.0 °C |
19.2 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 8.00 J | 5.90 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 87.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
48.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
50.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C | 194 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 108 °C @Thickness 3.20 mm |
226 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 56.0 °C @Thickness 3.20 mm |
133 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 10 ohm - 1e+05 | 10 ohm - 1e+05 | ASTM D257 |
Users viewing this material also viewed the following:
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 1.0 PHR MBT
- Samyang Trihip® B500 High Impact Polystyrene
- Vyncolit Vyntec® CF8050 Carbon Fiber Reinforced Phenolic
- Loctite® 3440 1 component Gold/polymer filler Anisotropic Epoxy Adhesive
- Chengdu Polyster 4502 High Performance Grade TPV
- Arkema Group Rilsan® AESN Y T6L Nylon 12, MoS2 Filled (Conditioned)
- Arlon 55503R062 0.062" Cured Silicone Rubber with Fiberglass Substrate
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 2.5 PHR Vul-Cup 40KE Peroxide
- DSM Arnite® T06 202 PBT (European and Asian Grade)
Copyright © lookpolymers.com All Rights Reserved