SABIC Innovative Plastics LNP STAT-KON KX97157 Acetal Copolymer (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP STAT-KON
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP STAT-KON KX97157 Acetal Copolymer (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* STATKON* KX97157 is a compound based on Acetal resin containing Carbon. Added features include : Electrically Conductive, Impact Modified.
Physical Properties Metric English Comments
Density 1.46 g/cc
0.0527 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0012 cm/cm
0.0012 in/in
SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength at Break 84.0 MPa
12200 psi
5 mm/min; ISO 527
Elongation at Break 0.70 %
0.70 %
5 mm/min; ISO 527
1.7 %
1.7 %
Flexural Strain, break, 2 mm/min; ISO 178
Tensile Modulus 13.1 GPa
1900 ksi
1 mm/min; ISO 527
Flexural Strength 89.0 MPa
12900 psi
2 mm/min; ISO 178
Flexural Yield Strength 96.0 MPa
13900 psi
2 mm/min; ISO 178
Flexural Modulus 9.60 GPa
1390 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
80*10*4; ISO 180/1A
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 32.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 17.8 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 98.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 54.4 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 152 °C
306 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
Electrical Properties Metric English Comments
Surface Resistance 10 - 1000 ohm
10 - 1000 ohm
ASTM D257