SABIC Innovative Plastics LNP STAT-KON EX02598C PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON EX02598C PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* EX02598C is a compound based on Polyetherimide containing Proprietary Filler(s). Added features of this material include: Clean Compound System, Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 |
| Density | 1.26 g/cc | 0.0455 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 52.0 MPa | 7540 psi | Type I, 5 mm/min; ASTM D638 |
| 60.0 MPa | 8700 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 1.7 % | 1.7 % | Type I, 5 mm/min; ASTM D638 |
| 2.1 % | 2.1 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 3.24 GPa | 470 ksi | 1 mm/min; ISO 527 |
| 3.41 GPa | 495 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 72.0 MPa | 10400 psi | ISO 178 |
| 98.0 MPa | 14200 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 3.11 GPa | 451 ksi | 2 mm/min; ISO 178 |
| 3.31 GPa | 480 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.190 J/cm | 0.356 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.66 J/cm | 4.98 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² | 0.952 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 18.0 kJ/m² | 8.57 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 2.00 J @Temperature 23.0 °C |
1.48 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
27.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 54.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
30.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 171 °C | 340 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 172 °C @Thickness 3.20 mm |
342 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 163 °C @Thickness 3.20 mm |
325 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 3.0 - 6.0 ohm | 3.0 - 6.0 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® CY2010 PC+ABS (Europe-Africa-Middle East)
- SABIC Innovative Plastics Lexan® EXL1494T PC Copolymer (Asia Pacific)
- SABIC Innovative Plastics Lexan® EXL1810T PC Copolymer
- Dow Questra® WA202 High Heat Syndiotactic Polystyrene, 30% Glass Filled (discontinued **)
- Polimeri Europa EDISTIR PD RR745E High Impact Polystyrene (HIPS) (discontinued **)
- SABIC Innovative Plastics Valox® V3900WX PBT+PC (Asia Pacific)
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber, 0.20 PHR Caytur 4
- Covestro Makrolon® OD2015 Polycarbonate
- Buckeye Polymers BP PPC 0212 R Reprocessed Polypropylene, Unfilled
- ExxonMobil Santoprene® 8291-60B500 Thermoplastic Vulcanizate (discontinued **)
Copyright © lookpolymers.com All Rights Reserved