- Aremco Ceramabond™ 571 High Temperature Ceramic Adhesive/Paste, Magnesium Oxide Filled
Aremco Ceramabond™ 571 High Temperature Ceramic Adhesive/Paste, Magnesium Oxide Filled
| Category | Ceramic , Oxide , Magnesium Oxide |
| Manufacturer | Aremco |
| Trade Name | Ceramabond™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aremco Ceramabond™ 571 High Temperature Ceramic Adhesive/Paste, Magnesium Oxide Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Aremco's ceramic adhesives are easy to use, one- and two-component systems which air dry in 1-2 hrs and are ready for use following a 200 to 700 °F cure. These materials are mostly water-based and do not outgas after curing. They are also environmentally safe, non-flammable materials which contain no volatile organic compounds.General Features: Dielectric, High Strength Bonding: Ceramic to Metal, Metal to Metal Principal Use: Heaters, Sensors
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.90 - 2.20 g/cc | 0.0686 - 0.0795 lb/in³ | |
| Volatile Organic Compounds (VOC) Content | 0.000 g/l | 0.000 g/l | |
| Viscosity | 20000 - 90000 cP | 20000 - 90000 cP |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Impact Test | 29.8 J | 22.0 ft-lb | Torque Strength; curing at 1000°F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 12.6 µm/m-°C | 7.00 µin/in-°F | |
| Maximum Service Temperature, Air | 1760 °C | 3200 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 3.58 kV/mm | 91.0 kV/in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 50.0 - 90.0 °C | 122 - 194 °F | Application Temp |
| Cure Time | 120 min @Temperature 93.3 °C |
2.00 hour @Temperature 200 °F |
preceeded by 1-4 hour air set |
| Shelf Life | 6.00 Month @Temperature 4.44 - 32.2 °C |
6.00 Month @Temperature 40.0 - 90.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Acid Resistance | Fair | after curing at 700°F for 2 hours |
| Alkali Resistance | Good | after curing at 700°F for 2 hours |
| Color | Off-White | |
| Mix Ratio | 1:1, 1.5:1 | powder:liquid |
| Moisture Resistance | Excellent | after curing at 700°F for 2 hours |
| Solvent | Water | |
| Thinner | 571-T |
Users viewing this material also viewed the following:
- Oxford Polymers PP-Homopolymer-20GF-Natural PP, 20% Glass Fiber Reinforced
- Ineos ABS Lustran® QE 1094 AS General Purpose, High-Impact (discontinued **)
- Ravago Manufacturing Americas Hylon® N1000STHL HF Nylon 6/6 (discontinued **)
- Lubrizol Advanced Materials Pearlbond® DAP 750/2 Thermoplastic Polyurethane
- Gwent Electronic Materials P2121112P9 Tetrafluoromethane Plasma Modified Multiwalled Carbon Nanotubes
- Zircar Ceramics SI-RIG Silica Rigidizer
- A. Schulman POLYAXIS® PD2000 Polypropylene
- Loctite® Varidot™ 3617 Stencil Print
- Crucible Steel 304L Chromium-Nickel Steel
- Polykemi AB POLYfill PPH GF10020 PD2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled
Copyright © lookpolymers.com All Rights Reserved