SABIC Innovative Plastics LNP STAT-KON DE003Z PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DE003Z PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STAT-KON* DE003Z is a compound based on Polycarbonate resin containing 15% Carbon Fiber. Added features of this material include: Electrically Conductive, Extrusion Grade.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.26 g/cc | 1.26 g/cc | ASTM D792 |
| Density | 1.253 g/cc | 0.04527 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.130 % | 0.130 % | 50% RH, 24 hrs; ASTM D570 |
| 0.210 % | 0.210 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 130 MPa | 18900 psi | 5 mm/min; ISO 527 |
| 134 MPa | 19400 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 134 MPa | 19400 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 2.4 % | 2.4 % | Type I, 5 mm/min; ASTM D638 |
| 2.6 % | 2.6 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 10.66 GPa | 1546 ksi | 1 mm/min; ISO 527 |
| 11.32 GPa | 1642 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 191 MPa | 27700 psi | ISO 178 |
| 200 MPa | 29000 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 9.12 GPa | 1320 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 9.29 GPa | 1350 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.980 J/cm | 1.84 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.23 J/cm | 11.7 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 39.0 kJ/m² | 18.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 24.0 J @Temperature 23.0 °C |
17.7 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 22.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
12.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 48.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
26.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 147 °C | 297 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 147 °C @Thickness 3.20 mm |
297 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 143 °C | 289 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 144 °C @Thickness 3.20 mm |
291 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Karina E 817-48/1-F-ERYBT Black PVC Compound
- Spartech UltraTuf SP-7010 Polycarbonate Sheet
- SABIC Innovative Plastics Xenoy® EXXY0113 PBT (Europe-Africa-Middle East)
- Wieland Porta REFLEX® PFM Alloy
- Eastman Eastar GN119 Copolyester
- DuPont Performance Polymers Crastin® 6131 NC010 Polybutylene Terephthalate (PBT) (Unverified Data**)
- Eurotec® Tecomid® NB40 GR20 NL XA60 PA6, 20% glass fiber reinforced, flame retardant - halogen & red phosphorus free, heat stabilized, natural
- Axiall 4501 Flexible PVC
- Polyram RamOfin PPC104 Polypropylene Copolymer
Copyright © lookpolymers.com All Rights Reserved