SABIC Innovative Plastics LNP STAT-KON DD0009PC PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DD0009PC PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STAT-KON* DD0009PC is a compound based on Polycarbonate resin containing Carbon Powder, Flame Retardant. Added features of this material include: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0600 % | 0.0600 % | 23°C / 50% RH; ISO 62 |
| 0.170 % | 0.170 % | 50% RH, 24 hrs; ASTM D570 | |
| Linear Mold Shrinkage, Flow | 0.0066 cm/cm @Time 86400 sec |
0.0066 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0055 cm/cm @Time 86400 sec |
0.0055 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 46.0 MPa | 6670 psi | ISO 527 |
| 50.0 MPa | 7250 psi | ASTM D638 | |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | ISO 527 |
| 60.0 MPa | 8700 psi | ASTM D638 | |
| Elongation at Break | 10.8 % | 10.8 % | ASTM D638 |
| 11.3 % | 11.3 % | ISO 527 | |
| Elongation at Yield | 4.7 % | 4.7 % | ISO 527 |
| 4.9 % | 4.9 % | ASTM D638 | |
| Tensile Modulus | 2.61 GPa | 379 ksi | 1 mm/min; ISO 527 |
| 2.64 GPa | 383 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 95.0 MPa | 13800 psi | ASTM D790 |
| 95.0 MPa | 13800 psi | ISO 178 | |
| Flexural Modulus | 2.57 GPa | 373 ksi | ASTM D790 |
| 2.61 GPa | 379 ksi | ISO 178 | |
| Izod Impact, Notched | 2.79 J/cm | 5.23 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 21.6 J/cm | 40.5 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 131 kJ/m² | 62.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 37.0 J | 27.3 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 65.0 J | 47.9 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C @Thickness 3.20 mm |
284 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 126 °C | 259 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 127 °C @Thickness 3.20 mm |
261 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 6.50e+10 ohm | 6.50e+10 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P3970 TPE, PP Overmold or Standalone use
- Overview of materials for Acrylonitrile Butadiene Styrene (ABS), 30% Carbon Fiber Filled
- Greene Tweed Orthetek® WF Polyketone, Continuous Woven Carbon Fiber
- Teknor Apex Telcar® TL-3050-88 Thermoplastic Elastomer
- ExxonMobil Exterex™ A51 Synthetic Fluid
- Fainplast Compounds KL 0209 Flexible PVC, Insulation for High Temperatures Lead Free
- Ascend Performance Materials Vydyne® 47H Nylon 66, Impact Modified, Conditioned
- Cheng Yu Plastic E2315 Flame Retardant PET, 15% Glass Fiber
- ATI Allegheny Ludlum Martensitic Stainless Steel Type 410, Hardened + 538°C Temper
Copyright © lookpolymers.com All Rights Reserved