SABIC Innovative Plastics LNP STAT-KON 9X04323 PPE+PA66 (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON 9X04323 PPE+PA66 (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Stat-kon* 9X04323 is a compound based on Noryl GTX resin,Added features of this material include: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in³ | ASTM D792 |
| 1.11 g/cc | 0.0401 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.200 % | 0.200 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0093 - 0.0124 cm/cm @Time 86400 sec |
0.0093 - 0.0124 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 56.0 MPa | 8120 psi | Type I, 5 mm/min; ASTM D638 |
| 58.0 MPa | 8410 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 59.0 MPa | 8560 psi | Type I, 5 mm/min; ASTM D638 |
| 59.0 MPa | 8560 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 3.5 % | 3.5 % | 5 mm/min; ISO 527 |
| 3.7 % | 3.7 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 3.5 % | 3.5 % | 5 mm/min; ISO 527 |
| 3.7 % | 3.7 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 2.76 GPa | 400 ksi | 50 mm/min; ASTM D638 |
| 2.78 GPa | 403 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 99.0 MPa | 14400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 96.0 MPa | 13900 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.40 GPa | 348 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.59 GPa | 376 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 22.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
12.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 24.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
13.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 181 °C | 358 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 180 °C @Thickness 3.20 mm |
356 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 163 °C | 325 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 168 °C @Thickness 3.20 mm |
334 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 - 10000 ohm | 100 - 10000 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Victrex® PEEK 150P Polyetheretherketone, Unreinforced
- SABIC Innovative Plastics LNP LUBRICOMP KAL22 Acetal Copolymer (Europe-Africa-Middle East)
- Taiwan Sheen Soon Sheenthane® A9313H Thermoplastic Polyurethane Elastomer
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 80 PHR Mistron Vapor Filler
- Zircar Zirconia ZYW-15 Zirconia Cloth Insulation
- DSM Akulon® K224-LG6 Nylon 6-30% Glass Reinforced (European and Asian Grade) (Dry)
- Domo Domamid® 34 Polyamide 6
- Covestro Makrofol® BL 6-2 820802 Polycarbonate
- ATI Allegheny Ludlum AL 29-4-2® Duplex Stainless Steel, UNS S44800
- Gromax PBT 1200-211M
Copyright © lookpolymers.com All Rights Reserved