- Cresset Powers Cress-Alon™ NE6040-ST 4% Nano Clay Loaded, 6.0 r.v. Super Tough Grade Nylon 6, 50% RH
Cresset Powers Cress-Alon™ NE6040-ST 4% Nano Clay Loaded, 6.0 r.v. Super Tough Grade Nylon 6, 50% RH
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Cresset Powers, Ltd |
| Trade Name | Cress-Alon™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cresset Powers Cress-Alon™ NE6040-ST 4% Nano Clay Loaded, 6.0 r.v. Super Tough Grade Nylon 6, 50% RH.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Surpasses super tough neat resins in strength, heat resistance, and hardness.Information provided by Cresset Powers Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.064 g/cc | 0.03844 lb/in³ | ASTM D792 |
| Viscosity Measurement | 6.0 | 6.0 | Relative Viscosity |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | ASTM D638 |
| Elongation at Break | 182 % | 182 % | ASTM D638 |
| Izod Impact, Notched | 10.94 J/cm | 20.50 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | ASTM DSC |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 223R PC (Asia Pacific)
- Nye Lubricants UniFlor 8920U (491UV) (UF) Synthetic Oil
- Huntsman XU 442 Phenalkamine Hardener
- Techmer ES Luriblend® PA6 TSX10 Nylon 6
- Saint-Gobain COHRlastic® CF4444 Reversion Resistant Reinforced Solid Rubber
- Plenco 2408 Phenolic, Granular, Compression Molded
- A. Schulman LP390-01 Narrow Molecular Weight Copolymer
- Dow Corning RD ANTIFOAM EMULSION
- 3M FL029 Indoor UL Recognized Lexan Label Products
- Latrobe Lescalloy® HY-180 VIM-VAR ; 4.01 - 8.00 thickness High Strength Alloy Steel
Copyright © lookpolymers.com All Rights Reserved