SABIC Innovative Plastics LNP Lubriloy Z2000 PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Lubriloy |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Lubriloy Z2000 PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubriloy* Z2000 is a compound based on PPE+PS Blend resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D 792 |
| 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 | |
| Moisture Absorption at Equilibrium | 0.070 % | 0.070 % | 23°C / 50% RH; ISO 62 |
| 0.060 % @Time 86400 sec |
0.060 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0089 cm/cm @Time 86400 sec |
0.0089 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0089 cm/cm @Time 86400 sec |
0.0089 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0115 cm/cm @Time 86400 sec |
0.0115 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0115 cm/cm @Time 86400 sec |
0.0115 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 41.0 MPa | 5950 psi | ISO 527 |
| 42.0 MPa | 6090 psi | ASTM D 638 | |
| Tensile Strength, Yield | 38.0 MPa | 5510 psi | ISO 527 |
| 46.0 MPa | 6670 psi | ASTM D 638 | |
| Elongation at Break | 37.3 % | 37.3 % | ISO 527 |
| 52.3 % | 52.3 % | ASTM D 638 | |
| Elongation at Yield | 3.2 % | 3.2 % | ISO 527 |
| 4.2 % | 4.2 % | ASTM D 638 | |
| Tensile Modulus | 1.81 GPa | 263 ksi | 1 mm/min; ISO 527 |
| 1.82 GPa | 264 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 58.0 MPa | 8410 psi | ISO 178 |
| 74.0 MPa | 10700 psi | ASTM D 790 | |
| Flexural Modulus | 1.86 GPa | 270 ksi | ISO 178 |
| 2.08 GPa | 302 ksi | ASTM D 790 | |
| Izod Impact, Notched | 1.06 J/cm @Temperature 23.0 °C |
1.99 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 20.34 J/cm @Temperature 23.0 °C |
38.11 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² @Temperature 23.0 °C |
5.23 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 172 kJ/m² @Temperature 23.0 °C |
81.8 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.19 | 0.19 | ASTM D 3702 Modified |
| Coefficient of Friction, Static | 0.24 | 0.24 | ASTM D 3702 Modified |
| K (wear) Factor | 244 x 10-8 mm³/N-M | 121 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D 3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 81.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
45.5 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 82.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
45.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 88.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
49.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 89.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
49.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 138 °C | 280 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 140 °C @Thickness 3.20 mm |
284 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 121 °C @Thickness 3.20 mm |
250 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Nye Lubricants 782KA (NG) Synthetic Oil
- Radici Heraflex® A 65 31 I HW TPS-SEBS Thermoplastic Elastomer
- Lehmann & Voss LUVOCOM® 1106-8154/GY Polyether imide, unreinforced, laser markable
- SolVin 386NB Polyvinyl Chloride Low Viscosity Paste
- Westlake EP310 Low Density Polyethylene
- Dandong Taico Minerals TAICOCITE® TC50 Magnesium Hydroxide
- Barlog Plastics KEBALLOY EP 23 ABS/PC, unreinforced, electro platable grade
- Ametek High Purity Nickel Strip 899L 3/4 Hard
- 3M FP011 Clear Polypropylene Label Products
- Resinlab® TL5072 Anaerobic Threadlocking Compound
Copyright © lookpolymers.com All Rights Reserved