SABIC Innovative Plastics LNP Lubricomp YP003 TPEE

Category Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyether Ester Elastomer
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Lubricomp YP003 TPEE.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP LUBRICOMP* YP003 is a compound based on TPEE resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 1.27 g/cc
0.0459 lb/in³
ASTM D 792
1.27 g/cc
0.0459 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.50 %
0.50 %
23°C / 50% RH; ISO 62
0.37 %

@Time 86400 sec
 0.37 %

@Time 24.0 hour
 50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.021 cm/cm

@Time 86400 sec
 0.021 in/in

@Time 24.0 hour
 ASTM D 955
0.0213 cm/cm

@Time 86400 sec
 0.0213 in/in

@Time 24.0 hour
 ISO 294
Linear Mold Shrinkage, Transverse 0.020 cm/cm

@Time 86400 sec
 0.020 in/in

@Time 24.0 hour
 ASTM D 955
0.0205 cm/cm

@Time 86400 sec
 0.0205 in/in

@Time 24.0 hour
 ISO 294
Mechanical Properties Metric English Comments
Tensile Strength, Yield 13.0 MPa
1890 psi
ASTM D 638
14.0 MPa
2030 psi
ISO 527
Elongation at Yield 39.9 %
39.9 %
ISO 527
53.5 %
53.5 %
ASTM D 638
Tensile Modulus 0.200 GPa
29.0 ksi
50 mm/min; ASTM D 638
0.240 GPa
34.8 ksi
1 mm/min; ISO 527
Flexural Modulus 0.260 GPa
37.7 ksi
ASTM D 790
0.270 GPa
39.2 ksi
ISO 178
Izod Impact, Notched 2.40 J/cm

@Temperature 23.0 °C
 4.50 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 ASTM D 4812
Izod Impact, Notched (ISO) 27.0 kJ/m²

@Temperature 23.0 °C
 12.8 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Impact Test 26.0 J
19.2 ft-lb
Multiaxial Impact; ISO 6603
27.0 J

@Temperature 23.0 °C
 19.9 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Energy @ peak; ASTM D 3763
Coefficient of Friction, Dynamic 0.47
0.47
ASTM D 3702 Modified
Coefficient of Friction, Static 0.45
0.45
ASTM D 3702 Modified
K (wear) Factor 10.1 x 10-8 mm³/N-M
5.00 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D 3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 111 µm/m-°C

@Temperature -40.0 - 40.0 °C
 61.7 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
111 µm/m-°C

@Temperature -40.0 - 40.0 °C
 61.7 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 184 µm/m-°C

@Temperature -40.0 - 40.0 °C
 102 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
184 µm/m-°C

@Temperature -40.0 - 40.0 °C
 102 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 47.0 °C

@Thickness 3.20 mm
 117 °F

@Thickness 0.126 in
 unannealed; ASTM D 648