SABIC Innovative Plastics LNP Lubricomp RL0049 PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, PTFE Filled |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Lubricomp RL0049 PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* RL0049 is a compound based on Nylon 66 resin containing PTFE, Flame Retardant. Added features of this material include: Internally Lubricated, Flame Retardant.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.53 g/cc | 0.0553 lb/in³ | ASTM D 792 |
| Moisture Absorption at Equilibrium | 0.30 % @Time 86400 sec |
0.30 % @Time 24.0 hour |
50% RH; ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.015 cm/cm @Time 86400 sec |
0.015 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0152 cm/cm @Time 86400 sec |
0.0152 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0167 cm/cm @Time 86400 sec |
0.0167 in/in @Time 24.0 hour |
ISO 294 |
| 0.017 cm/cm @Time 86400 sec |
0.017 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 46.0 MPa | 6670 psi | ASTM D 638 |
| 46.0 MPa | 6670 psi | ISO 527 | |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 |
| 2.2 % | 2.2 % | ASTM D 638 | |
| Tensile Modulus | 3.16 GPa | 458 ksi | 1 mm/min; ISO 527 |
| 3.17 GPa | 460 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 75.0 MPa | 10900 psi | ASTM D 790 |
| 79.0 MPa | 11500 psi | ISO 178 | |
| Flexural Modulus | 2.97 GPa | 431 ksi | ISO 178 |
| 3.09 GPa | 448 ksi | ASTM D 790 | |
| Izod Impact, Notched | 0.210 J/cm @Temperature 23.0 °C |
0.393 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 1.60 J/cm @Temperature 23.0 °C |
3.00 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² @Temperature 23.0 °C |
0.952 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 10.0 kJ/m² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| 1.00 J @Temperature 23.0 °C |
0.738 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 95.0 °C @Thickness 3.20 mm |
203 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- S&E Specialty Polymers TufFill™ 5701 Black PP
- SABIC Innovative Plastics Lexan® EXL1132T PC Copolymer
- Lehmann & Voss LUVOCOM® 1105-7751 PEEK, with carbon fiber, easy flowing
- M Chemical GUARD DOGâ„¢ UV234 Light Absorber, Benzotriazole Derivative
- PlastxWorld CEVIAN® B5526 30% GF PBT/ABS Alloy
- Chase Plastics CP Pryme® N313GL (DAM) Nylon 6 (Utility Grade), 13% Glass Fiber Reinforced, Internally Lubricated
- ChevronTexaco Regular Unleaded Gasoline
- Azoty Tarnow™ Alphalon™ 36 Nylon 6
- Henkel SynSpand 9835 Expanding Syntactic Film
Copyright © lookpolymers.com All Rights Reserved