SABIC Innovative Plastics LNP Lubricomp EFP36G PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Lubricomp EFP36G PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* EFP36G is a Polyetherimide base resin containing a Mixed Glass Fiber and PTFE/Silicone.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.59 g/cc | 0.0574 lb/in³ | ISO 1183 |
| 1.59 g/cc | 0.0574 lb/in³ | ASTM D 792 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 96.0 MPa | 13900 psi | 5 mm/min; ISO 527 |
| 107 MPa | 15500 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 1.7 % | 1.7 % | 5 mm/min; ISO 527 |
| 2.2 % | 2.2 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 11.44 GPa | 1659 ksi | 50 mm/min; ASTM D 638 |
| 11.76 GPa | 1706 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 161 MPa | 23400 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 164 MPa | 23800 psi | ISO 178 | |
| Flexural Modulus | 8.45 GPa | 1230 ksi | 2 mm/min; ISO 178 |
| 8.58 GPa | 1240 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.760 J/cm @Temperature 23.0 °C |
1.42 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 4.08 J/cm @Temperature 23.0 °C |
7.64 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² @Temperature 23.0 °C |
14.3 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| 12.0 J @Temperature 23.0 °C |
8.85 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 | |
| Coefficient of Friction, Dynamic | 0.49 | 0.49 | ASTM D 3702 Modified |
| Coefficient of Friction, Static | 0.60 | 0.60 | ASTM D 3702 Modified |
| K (wear) Factor | 119 x 10-8 mm³/N-M | 59.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D 3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 39.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
21.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| CTE, linear, Transverse to Flow | 22.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
12.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 204 °C | 399 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 202 °C @Thickness 3.20 mm |
396 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 209 °C @Thickness 3.20 mm |
408 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PH 51 N PP, basic type
- Protective Coating PC-Lumber™ Epoxy Putty
- Indium Corp. Standard ITO Indium Tin Oxide
- SABIC Innovative Plastics LNP LUBRICOMP WFL369 PBT (Asia Pacific)
- Solvay Specialty Polymers Ryton® QA200P Polyphenylene Sulfide (PPS)
- Master Bond LED401 One Component LED Curable Adhesive System
- Zhejiang Juner PA-A5 Flame-Retardant & Mineral Reinforced PA6
- Loctite® 414 General Purpose Ethyl Cyanoacrylate Bonding Adhesive
Copyright © lookpolymers.com All Rights Reserved