NYCOA 512 PA 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced, Flame Retardant |
| Manufacturer | NYCOA, Inc. |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NYCOA 512 PA 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
UL and NSF rated nucleated general purpose molding gradeInformation provided by NYCOA, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792 |
| Water Absorption | 1.7 % | 1.7 % | ASTM D570 |
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 86.0 MPa | 12500 psi | ASTM D638 |
| Elongation at Break | >= 40 % | >= 40 % | ASTM D638 |
| Flexural Yield Strength | 99.0 MPa | 14400 psi | ASTM D790 |
| Flexural Modulus | 2.656 GPa | 385.2 ksi | ASTM D790 |
| Izod Impact, Notched | 0.460 J/cm | 0.862 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 221 °C | 430 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | ASTM D648 |
| Flammability, UL94 | V-2 @Thickness 0.700 mm |
V-2 @Thickness 0.0276 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 250 °C | 482 °F | |
| Rear Barrel Temperature | 225 °C | 437 °F | |
| Middle Barrel Temperature | 230 °C | 446 °F | |
| Front Barrel Temperature | 250 °C | 482 °F | |
| Nozzle Temperature | 250 °C | 482 °F | |
| Mold Temperature | 80.0 °C | 176 °F | |
| Drying Temperature | 76.0 °C | 169 °F |
Users viewing this material also viewed the following:
- Precision Polymer Engineering Perlast® G67P Translucent Perfluoroelastomer
- Potters Industries A-Series Premium 1.5MM Soda-Lime Silica Technical Quality Solid Glass Spheres
- Polykemi AB POLYfill PPH T2040 Polypropylene Homopolymer, Mineral Reinforced
- Industeel CLC 1.2312 Prehardened Mold Steel (300HB/32HRC) with Improved Machinability
- Indium Corp. Indalloy® 264 Tin-Antimony Solder Alloy
- ChevronTexaco HS Diesel 2
- BASF Heligoen® Green L 9361 Color Additive
- Arlon 44560R010 0.010" (0.254 mm) Uncured Silicone Rubber with Fiberglass Substrate
- Ashley Polymers Ashlene® RH180 Acetal
- A. Schulman POLYFORT™ PP 3701
Copyright © lookpolymers.com All Rights Reserved