SABIC Innovative Plastics LNP LUBRILOY Z2000 PPE+PS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Lubriloy |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRILOY Z2000 PPE+PS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubriloy* Z2000 is a compound based on PPE+PS Blend resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792 |
| 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.0600 % | 0.0600 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0700 % | 0.0700 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0089 cm/cm @Time 86400 sec |
0.0089 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0089 cm/cm @Time 86400 sec |
0.0089 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0115 cm/cm @Time 86400 sec |
0.0115 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0115 cm/cm @Time 86400 sec |
0.0115 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 41.0 MPa | 5950 psi | ISO 527 |
| 42.0 MPa | 6090 psi | ASTM D638 | |
| Tensile Strength, Yield | 38.0 MPa | 5510 psi | ISO 527 |
| 46.0 MPa | 6670 psi | ASTM D638 | |
| Elongation at Break | 37.3 % | 37.3 % | ISO 527 |
| 52.3 % | 52.3 % | ASTM D638 | |
| Elongation at Yield | 3.2 % | 3.2 % | ISO 527 |
| 4.2 % | 4.2 % | ASTM D638 | |
| Tensile Modulus | 1.81 GPa | 263 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 58.0 MPa | 8410 psi | ISO 178 |
| 74.0 MPa | 10700 psi | ASTM D790 | |
| Flexural Modulus | 1.86 GPa | 270 ksi | ISO 178 |
| 2.08 GPa | 302 ksi | ASTM D790 | |
| Izod Impact, Notched | 1.06 J/cm | 1.99 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 20.34 J/cm | 38.11 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 172 kJ/m² | 81.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.19 | 0.19 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.24 | 0.24 | ASTM D3702 Modified |
| K (wear) Factor | 244 x 10-8 mm³/N-M | 121 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 81.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
45.5 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 82.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
45.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 88.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
49.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 89.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
49.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 138 °C | 280 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 140 °C @Thickness 3.20 mm |
284 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 121 °C @Thickness 3.20 mm |
250 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- NanoAmor 95%, OD/ID: 8-15/3-5 nm Aligned Multi-Walled Carbon Nanotubes
- Overview of materials for Acetal Copolymer, Unreinforced
- Mitsui UNISTOLEâ„¢ P-902M Polyolefinic Primer/ Adhesive
- SMAC CABLE® 2524S-20-08 Damping Material
- Lubrizol Estane® T465A Thermoplastic Polyurethane
- A. Schulman POLYFORT™ FPP 1640 Glass Reinforced, Mineral Fortified Homopolymer Polypropylene
- Esstech X-829-0050 Adhesive Monomer PMGDM, 50% (w/w) Solution in Acetone, C32H34O16
- Carpenter Stentor® Alloy Tool Steel (Oil-Hard) (AISI 02)
- A. Schulman SCHULADUR® A GF33HI 33% Glass Fiber Reinforced, High Impact PBT
- SABIC Innovative Plastics LNP THERMOCOMP PH0460A PA 6 (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved