SABIC Innovative Plastics LNP LUBRILOY UA200A PPA
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Lubriloy |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRILOY UA200A PPA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRILOY* UA200A is a compound based on Polyphthalamide resin containing Aramid Fiber, Proprietary Lubricant. Added feature of this material is: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.420 % | 0.420 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0090 - 0.011 cm/cm @Time 86400 sec |
0.0090 - 0.011 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.014 - 0.016 cm/cm @Time 86400 sec |
0.014 - 0.016 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 86.0 MPa | 12500 psi | ASTM D638 |
| Elongation at Break | 3.3 % | 3.3 % | ASTM D638 |
| Tensile Modulus | 4.29 GPa | 622 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 131 MPa | 19000 psi | ASTM D790 |
| Flexural Modulus | 3.72 GPa | 540 ksi | ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.03 J/cm | 11.3 ft-lb/in | ASTM D4812 |
| Coefficient of Friction, Dynamic | 0.25 | 0.25 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.21 | 0.21 | ASTM D3702 Modified |
| K (wear) Factor | 10.1 x 10-8 mm³/N-M | 5.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 45.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
25.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 59.3 µm/m-°C @Temperature -40.0 - 40.0 °C |
32.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Thermal Conductivity | 0.290 W/m-K | 2.01 BTU-in/hr-ft²-°F | ASTM E 1530 |
| Deflection Temperature at 0.46 MPa (66 psi) | 253 °C @Thickness 3.20 mm |
487 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 118 °C @Thickness 3.20 mm |
244 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Solvay Specialty Polymers Veradel® 3000RP Polyethersulfone (PESU)
- Silon Taborex TA 2126 HD Catalyst Masterbatch
- A. Schulman PP 3476 Polypropylene Homopolymer Polypropylene
- Hexcel® HexPly® F522 Epoxy Resin, K120 Kevlar® Fabric
- American Elements A-MITE™ Aluminum Oxide Nanopowder
- Eagle Brass 260 Cartridge Brass, 1/2 Hard
- Arlon 30300R062 0.062" (1.57 mm) Uncured Silicone Rubber on Kodacel Carrier
- Arlon 55576R060 0.060" Cured/Uncured Silicone Rubber with Fiberglass Substrate
- Saint-Gobain Chemfab® 183 PTFE Coated Fiberglass Conveyor Belting
Copyright © lookpolymers.com All Rights Reserved