ExxonMobil Exceed™ 2227ED Metallocene Polyethylene Resin (European Grade)

Category	Polymer , Thermoplastic , Polyethylene (PE)
Manufacturer	Exxon Chemical
Trade Name	Exceed™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Exceed™ 2227ED Metallocene Polyethylene Resin (European Grade).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: Exceed 2227ED is a metallocene ethylene-hexene copolymer. It offers an excellent balance of high modulus and impact strength. The higher melt index makes it ideally suited for LDPE rich blendsAvailability: Africa & Middle East and EuropeAdditive:Antiblock: 750 ppmSlip: 1250 ppm Processing Aid: Yes Thermal Stabilizer: Yes Applications:Blown Film Bread Bags Freezer Film Hygiene Film Overwrap FilmPackaging Films Information provided by ExxonMobil

Physical Properties	Metric	English	Comments
Density	0.927 g/cc	0.0335 lb/in³	ExxonMobil method
Melt Flow	2.2 g/10 min @Load 2.16 kg, Temperature 190 °C	2.2 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Antiblock Level	750 ppm	750 ppm
Slip Level	1250 ppm	1250 ppm

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	540 %	540 %	ASTM D882
Film Elongation at Break, TD	620 %	620 %	ASTM D882
Elmendorf Tear Strength MD	230 g	230 g	ASTM D1922
Elmendorf Tear Strength TD	450 g	450 g	ASTM D1922
Dart Drop Test	150 g	0.331 lb	ASTM D1709
Film Tensile Strength at Break, MD	40.0 MPa	5800 psi	ASTM D882
Film Tensile Strength at Break, TD	37.2 MPa	5400 psi	ASTM D882
1% Secant Modulus, MD	338 MPa	49000 psi	ASTM D882
1% Secant Modulus, TD	331 MPa	48000 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Melting Point	<= 253 °C	<= 487 °F	Peak Melting Point; ExxonMobil method

Optical Properties	Metric	English	Comments
Haze	6.0 %	6.0 %	ASTM D1003
Gloss	12 %	12 %	45°; ASTM D2457

Descriptive Properties	Value	Comments
Puncture Force	11 lbf	ExxonMobil Method