SABIC Innovative Plastics LNP LUBRICOMP UCL36S PPA (Asia Pacific)

Category	Polymer , Thermoplastic , Polyphthalamide (PPA)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP LUBRICOMP
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP LUBRICOMP UCL36S PPA (Asia Pacific).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* Lubricomp* UCL36S is a compound based on Polyphthalamide resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Heat Stabilized, Electrically Conductive.

Physical Properties	Metric	English	Comments
Density	1.41 g/cc	0.0509 lb/inÂ³	ASTM D792

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	214 MPa	31000 psi	ISO 527
	216 MPa	31300 psi	ASTM D638
Elongation at Break	1.2 %	1.2 %	ISO 527
	1.6 %	1.6 %	ASTM D638
Tensile Modulus	20.13 GPa	2920 ksi	50 mm/min; ASTM D638
Flexural Strength	324 MPa	47000 psi	ASTM D790
	334 MPa	48400 psi	ISO 178
Flexural Modulus	18.82 GPa	2730 ksi	ASTM D790
	22.7 GPa	3290 ksi	ISO 178
Izod Impact, Notched	0.960 J/cm	1.80 ft-lb/in	ASTM D256
Izod Impact, Unnotched	9.39 J/cm	17.6 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	8.00 kJ/mÂ²	3.81 ft-lb/inÂ²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	39.0 kJ/mÂ²	18.6 ft-lb/inÂ²	80104; ISO 180/1U
Coefficient of Friction, Dynamic	0.36	0.36	ASTM D3702 Modified
Coefficient of Friction, Static	0.27	0.27	ASTM D3702 Modified
K (wear) Factor	32.2 x 10^-8 mmÂ³/N-M	16.0 x 10^-10 inÂ³-min/ft-lb-hr	Washer; ASTM D3702 Modified

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	279 Â°C @Thickness 3.20 mm	534 Â°F @Thickness 0.126 in	unannealed; ASTM D648

Electrical Properties	Metric	English	Comments
Surface Resistance	100 - 1.00e+6 ohm	100 - 1.00e+6 ohm	ASTM D257