SABIC Innovative Plastics LNP LUBRICOMP RFN14 PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP RFN14 PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* RFN14 is a compound based on Nylon 66 containing 20% Glass Fiber, 5% MOS2. Added features of this grade include: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.33 g/cc | 1.33 g/cc | ASTM D792 |
| Density | 1.32 g/cc | 0.0477 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.670 % | 0.670 % | 50% RH, 24 hrs; ASTM D570 |
| 0.960 % | 0.960 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0060 cm/cm @Time 86400 sec |
0.0030 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.020 cm/cm @Time 86400 sec |
0.0080 - 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 134 MPa | 19400 psi | 5 mm/min; ISO 527 |
| 135 MPa | 19600 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.9 % | 1.9 % | Type I, 5 mm/min; ASTM D638 |
| 1.9 % | 1.9 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 8.52 GPa | 1240 ksi | 1 mm/min; ISO 527 |
| 8.85 GPa | 1280 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 204 MPa | 29600 psi | ISO 178 |
| 205 MPa | 29700 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 7.26 GPa | 1050 ksi | 2 mm/min; ISO 178 |
| 7.45 GPa | 1080 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.470 J/cm | 0.881 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.01 J/cm | 7.51 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 32.0 kJ/m² | 15.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 5.00 J @Temperature 23.0 °C |
3.69 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.41 | 0.41 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.45 | 0.45 | ASTM D3702 Modified |
| K (wear) Factor | 2.01 x 10-8 mm³/N-M | 1.00 x 10-10 in³-min/ft-lb-hr | Ring; ASTM D3702 Modified |
| 207 x 10-8 mm³/N-M | 103 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
22.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 78.1 µm/m-°C @Temperature -30.0 - 30.0 °C |
43.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 258 °C | 496 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 260 °C @Thickness 3.20 mm |
500 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 249 °C @Thickness 3.20 mm |
480 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- 3M Dyneon™ TF 5032R PTFE (discontinued **)
- LyondellBasell Adsylâ„¢ 5 X 37 F Polyolefin
- Shandong Dongyue Polymer TFP Tetrafluoropropanol
- SABIC Innovative Plastics LNP THERMOCOMP KF006XXC Acetal Copolymer (Asia Pacific)
- SABIC Innovative Plastics LNP THERMOTUF RF002I PA 66 (Asia Pacific)
- A. Schulman POLYBATCH™ Red 5557 Concentrate Based In Polyethylene
- Zotefoams Plastazote® LD28 Low Density Polyethylene Foam
- Chesterton MRS S2 Metal Rebuilding System
- BorsodChem ONGROSTYR F-III Expandable Polystyrene (EPS)
Copyright © lookpolymers.com All Rights Reserved