- TIMET 10-2-3 Titanium Alloy (Ti-10V-2Fe-3Al), Aged Billet/Bar per ASTM 4987
TIMET 10-2-3 Titanium Alloy (Ti-10V-2Fe-3Al), Aged Billet/Bar per ASTM 4987
| Category | Metal , Nonferrous Metal , Titanium Alloy , Beta Titanium Alloy |
| Manufacturer | TIMET |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | TIMET 10-2-3 Titanium Alloy (Ti-10V-2Fe-3Al), Aged Billet/Bar per ASTM 4987.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High-Strength Forging Alloy.Industry Specifications: USA Aerospace: AMS 4987.Features: A readily forgeable alloy that offers excellent combinations of strength, ductility, fracture toughness and high cycle fatigue strength. Typically used for critical aircraft structures, such as landing gear.Typical heat treatment for this alloy: Solution heat treat: 28-56°C below beta transus for a minimum for 30 mins, then water quench. Aging heat treatment: 482-593°C for 8 hrs, air cool.Data provided by TIMET.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 4.65 g/cc | 0.168 lb/in³ | Typical |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 1040 MPa | 151000 psi | Typical |
| Tensile Strength, Yield | 970 MPa @Strain 0.200 % |
141000 psi @Strain 0.200 % |
Typical |
| Elongation at Break | 15 % | 15 % | Typical |
| Reduction of Area | 20 % | 20 % | |
| Modulus of Elasticity | 103 GPa | 14900 ksi | Typical |
| Compressive Yield Strength | >= 924 MPa | >= 134000 psi | |
| Ultimate Bearing Strength | >= 1303 MPa | >= 189000 psi | e/D = 1.5 |
| >= 1579 MPa | >= 229000 psi | e/D = 2.0 | |
| Bearing Yield Strength | >= 1269 MPa | >= 184100 psi | e/D = 1.5 |
| >= 1462 MPa | >= 212000 psi | e/D = 2.0 | |
| Poissons Ratio | 0.32 | 0.32 | |
| Fatigue Strength | 780 MPa | 113000 psi | Limit; test specifics not reported |
| Fracture Toughness | >= 88.0 MPa-m½ | >= 80.1 ksi-in½ | ST then Aged 8 hrs |
| Shear Modulus | 42.1 GPa | 6110 ksi | |
| Shear Strength | >= 538 MPa | >= 78000 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 9.70 µm/m-°C @Temperature 20.0 °C |
5.39 µin/in-°F @Temperature 68.0 °F |
|
| Beta Transus | 800 °C | 1470 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | 2.6 - 3.4 % | 2.6 - 3.4 % | |
| Carbon, C | <= 0.050 % | <= 0.050 % | |
| Hydrogen, H | <= 0.015 % | <= 0.015 % | |
| Iron, Fe | 1.6 - 2.2 % | 1.6 - 2.2 % | |
| Nitrogen, N | <= 0.050 % | <= 0.050 % | |
| Oxygen, O | <= 0.13 % | <= 0.13 % | |
| Titanium, Ti | 83 - 86.8 % | 83 - 86.8 % | Calculated as remainder |
| Vanadium, V | 9.0 - 11 % | 9.0 - 11 % |
Users viewing this material also viewed the following:
- RheTech Products GC30P101-00 30% Glass Fiber Reinforced Polypropylene, Chemically Coupled, Natural
- SABIC B4660/B4660AB High Density Polyethylene for Blow Molding
- Michelman® Michem® Emulsion 94340 Nonionic polypropylene emulsion
- Karina E 10/31-RG-GE White Color Concentrate for PVC
- A. Schulman PP 3476 Polypropylene Homopolymer Polypropylene
- Daikin DAI-EL G-763 Fluoroelastomer Copolymer, Bisphenol Curable Grade, 66% Fluorine Content
- Alliance Polymers Zythane™ 6090A Thermoplastic Polyurethane Elastomer
- 3M Scotchcal™ ElectroCut™ 7725-96 Graphic Film
- BASF Sicotan® Yellow L 1012 Color Additive
- Polykemi AB POLYfill PPHC TS15020 Polypropylene, Mineral Reinforced
Copyright © lookpolymers.com All Rights Reserved