SABIC Innovative Plastics LNP LUBRICOMP RFL46ES PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP RFL46ES PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* RFL46ES is a compound based on Nylon 6/6 containing 30% Glass Fiber, 20% PTFE. Added features of this grade include: Wear Resistant, Heat Stabilized, Easy Molding.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.430 % | 0.430 % | 50% RH, 24 hrs; ASTM D570 |
| 0.820 % | 0.820 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm @Time 86400 sec |
0.0020 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.030 cm/cm @Time 86400 sec |
0.0090 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 145 MPa | 21000 psi | 5 mm/min; ISO 527 |
| 146 MPa | 21200 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.6 % | 2.6 % | Type I, 5 mm/min; ASTM D638 |
| 2.6 % | 2.6 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 10.42 GPa | 1511 ksi | 1 mm/min; ISO 527 |
| 10.88 GPa | 1578 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 221 MPa | 32100 psi | ISO 178 |
| 223 MPa | 32300 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 9.26 GPa | 1340 ksi | 2 mm/min; ISO 178 |
| 9.28 GPa | 1350 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.970 J/cm | 1.82 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.39 J/cm | 17.6 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 56.0 kJ/m² | 26.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.59 | 0.59 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.64 | 0.64 | ASTM D3702 Modified |
| K (wear) Factor | 24.2 x 10-8 mm³/N-M | 12.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 31.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
17.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 84.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
46.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 251 °C | 484 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 251 °C @Thickness 3.20 mm |
484 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 232 °C | 450 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 233 °C @Thickness 3.20 mm |
451 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® CM4219 PC+ABS (Asia Pacific)
- Solvay Specialty Polymers Algoflon® D 1610 F Polytetrafluoroethylene (PTFE)
- A. Schulman POLYBATCH™ Beige 60199 Concentrate Based In LLDPE
- ELASTO UK Dryflex® 662550S SEBS Based Material, Semi-Filled Qualities, 55A Hardness, Black
- DuPont™ Kapton® MT Polyimide Film
- ExxonMobil Isopar™ M (EU) Isoparaffin Fluid
- Epoxy Technology EPO-TEK® ED1020 Epoxy
- Arkema Group Rilsan® AECN TL Nylon 12, Cable Sheathing Grade (Dry)
Copyright © lookpolymers.com All Rights Reserved