- Imerys Allenâ„¢ G Kaolin
Imerys Allenâ„¢ G Kaolin
| Category | Ceramic , Clay , Kaolin Clay , Oxide , Aluminum Oxide , Silicon Oxide |
| Manufacturer | Imerys (Kentucky-Tennessee Clay Co.) |
| Trade Name | Allen™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Imerys Allenâ„¢ G Kaolin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Allen G is an intermediate-grained kaolin used as a suspension aid in ceramic glazes.Information provided by Imerys
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Particle Size | 0.50 µm | 0.50 µm | 28% finer than |
| 1.0 µm | 1.0 µm | 47% finer than | |
| 2.0 µm | 2.0 µm | 63% finer than | |
| 5.0 µm | 5.0 µm | 82% finer than | |
| 10 µm | 10 µm | 92% finer than | |
| 20 µm | 20 µm | 97% finer than | |
| Particle Mesh Size | 325 Mesh | 325 Mesh | 0.5% retained |
| pH | 5.5 | 5.5 | |
| Specific Surface Area | 13.5 m²/g | 13.5 m²/g |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.00207 GPa | 0.300 ksi | De-aired, Extruded, 50% Kaolin/50% Flint |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 38.5 % | 38.5 % | |
| CaO | 0.10 % | 0.10 % | |
| Carbon, C | 0.040 % | 0.040 % | |
| Fe2O3 | 0.50 % | 0.50 % | |
| K2O | 0.10 % | 0.10 % | |
| Loss on Ignition(%) | 13.6 % | 13.6 % | |
| MgO | 0.10 % | 0.10 % | |
| Na2O | 0.10 % | 0.10 % | |
| SiO2 | 45 % | 45 % | |
| Sulfur, S | 0.040 % | 0.040 % | |
| TiO2 | 1.5 % | 1.5 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| M.B.I. (meq/100g) | 3.5 |
Users viewing this material also viewed the following:
- Polimeri Europa Riblene® GM 30 R Low Density Polyethylene - Coating Grade
- SABIC Innovative Plastics Lexan® ML6076 PC
- Park Electrochemical Nelco® N4000-2 Multifunctional Epoxy Laminate and Prepreg
- Momentive Performance Materials Siloprenâ„¢ LSR 2645 Custom Liquid Silicone Rubber - Infant Care
- Haynes 625 alloy, 50% cold reduction, 1010°C anneal for 5 minutes
- Struktol CALCIUM STEARATE GR
- A. Schulman ComAlloy® E-14961 30% Glass Fiber Reinforced Polycarbonate
- DuPont Elvanol® 70-03 Polyvinyl Alcohol Fully Hydrolyzed General Purpose Grade
- Dow DOWLEX™ IP-10 High Density Polyethylene
- Dow XU 32019.10 Barrier Polymer
Copyright © lookpolymers.com All Rights Reserved