SABIC Innovative Plastics LNP LUBRICOMP RCL36 PA 66 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP RCL36 PA 66 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* RCL36 is a compound based on PA 66 resin containing PTFE, Carbon Fiber. Added features include: Electrically Conductive, Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 220 MPa | 31900 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.6 % | 1.6 % | 5 mm/min; ISO 527 |
| Flexural Yield Strength | 315 MPa | 45700 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 16.8 GPa | 2440 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 60.0 kJ/m² | 28.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 5.00 µm/m-°C @Temperature 23.0 - 60.0 °C |
2.78 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
44.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 251 °C | 484 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 10 - 1000 ohm | 10 - 1000 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® C4660 TPE, Transparent
- Greene Tweed Avalon® 87 PTFE, Glass Filled
- Haysite 42000 Polyester SMC, 22% Glass Reinforced
- Fiberfil® M-2501 BK Nylon 66, 40% mineral Filled, post industrial
- LATI Latilub 73/13-20T POM, PTFE Filled
- Shakespeare WP-550 diameter 0.5 mm Hydrolytically Stabilized Polyester Yarn
- UBE UBESTA® 3030U Nylon 12 (After Ethanol for 500 hours)
- Covestro Texin® 260 Urethane Thermoplastic Elastomer
- BASF Ultradur B 4300 G4 High Speed Unc. 20% Glass Filled PBT
Copyright © lookpolymers.com All Rights Reserved