SABIC Innovative Plastics LNP LUBRICOMP QCL34 PA6.10
| Category | Polymer , Thermoplastic , Nylon , Nylon 610 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP QCL34 PA6.10.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* QCL34 is a compound based on Nylon 6/10 resin containing 15% PTFE, 20% Carbon Fiber. Added features of this material include: Wear Resistant, Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 |
| Density | 1.27 g/cc | 0.0459 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.190 % | 0.190 % | 50% RH, 24 hrs; ASTM D570 |
| 0.300 % | 0.300 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.00060 - 0.00080 cm/cm @Time 86400 sec |
0.00060 - 0.00080 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 197 MPa | 28600 psi | 5 mm/min; ISO 527 |
| 201 MPa | 29200 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.6 % | 2.6 % | 5 mm/min; ISO 527 |
| 2.7 % | 2.7 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 15.56 GPa | 2257 ksi | 1 mm/min; ISO 527 |
| 16.6 GPa | 2410 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 280 MPa | 40600 psi | ISO 178 |
| 288 MPa | 41800 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 289 MPa | 41900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 12.4 GPa | 1800 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 12.49 GPa | 1812 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.05 J/cm | 1.97 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.44 J/cm | 15.8 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 52.0 kJ/m² | 24.7 ft-lb/in² | 80*10*3; ISO 180/1U |
| Dart Drop, Total Energy | 10.0 J @Temperature 23.0 °C |
7.38 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.39 | 0.39 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.33 | 0.33 | ASTM D3702 Modified |
| K (wear) Factor | 52.4 x 10-8 mm³/N-M | 26.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 21.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
11.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 58.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
32.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 221 °C | 430 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 212 °C @Thickness 3.20 mm |
414 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering V80G Fluoroelastomer Compound
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 60 PHR N220 Filler
- Mikro-Technik 75a Carboxymethylcellulose (CMC)
- Materion Beryllium Nickel Strip - Alloy 360 Hard
- Star Plastics PC/PET7901 Molding Grade PC/PET
- Ensinger TECAPRO™ SAN Polypropylene (PP)
- Bapolene® 270F Low Density Polyethylene Film Extrusion Resin
- Austin Novel Materials Texalan® 285A Polyester-based TPU