SABIC Innovative Plastics LNP LUBRICOMP PDX-U-05314 PPA (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP PDX-U-05314 PPA (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* PDX-U-05314 is a compound based on Polyphthalamide resin containing Proprietary Filler(s). Added features of this material include: Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.54 g/cc | 0.0556 lb/in³ | ASTM D792 |
| 1.55 g/cc | 0.0560 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.0032 cm/cm @Time 86400 sec |
0.0032 in/in @Time 24.0 hour |
ISO 294 |
| Linear Mold Shrinkage, Transverse | 0.0038 cm/cm @Time 86400 sec |
0.0038 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 108 MPa | 15700 psi | ISO 527 |
| 118 MPa | 17100 psi | ASTM D638 | |
| Elongation at Break | 1.7 % | 1.7 % | ISO 527 |
| 2.0 % | 2.0 % | ASTM D638 | |
| Tensile Modulus | 11.07 GPa | 1606 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 167 MPa | 24200 psi | ISO 178 |
| 186 MPa | 27000 psi | ASTM D790 | |
| Flexural Modulus | 10.59 GPa | 1536 ksi | ASTM D790 |
| Izod Impact, Notched | 0.580 J/cm | 1.09 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.48 J/cm | 8.39 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 50.0 kJ/m² | 23.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.39 | 0.39 | ASTM D3702 Modified |
| K (wear) Factor | 96.7 x 10-8 mm³/N-M | 48.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 21.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
12.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 55.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
31.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 250 °C @Thickness 3.20 mm |
482 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | V-0 @Thickness 1.80 mm |
V-0 @Thickness 0.0709 in |
UL 94 by SABIC-IP |
Users viewing this material also viewed the following:
- Park Electrochemical Nelco® NY9220 PTFE Laminate, Woven-Glass Reinforced
- PolyOne Bergamid™ B700 UF Polyamide 6 (Nylon 6)
- Heraeus Cleviosâ„¢ PH Conductive Sulfonate Polymer for Antistatic Coatings
- Samsung Cheil Industries Infino® GW-1041 PC/ABS, Unreinforced Recycled
- UBE UBESTA® 3030U Nylon 12 (After Hydrochloric Acid (10%) for 1000 hours)
- ExxonMobil Enable™ 20-10HA Metallocene Polyethylene Resin
- BNZ Materials Zelieblok 1900S Structural Ceramic Insulation
- Braskem F2022/0 LDPE Cast Film Extrusion Polyethylene
- Henkel Fixodine Z Surface Conditioner