SABIC Innovative Plastics LNP LUBRICOMP OCL36EXP PPS - LINEAR
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP OCL36EXP PPS - LINEAR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* OCL36EXP is a compound based on Linear PPS containing 30% Carbon Fiber, 15% PTFE. Added features of this grade include; Wear Resistant, Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc | ASTM D792 |
| Density | 1.56 g/cc | 0.0564 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0100 % | 0.0100 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0100 % | 0.0100 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 174 MPa | 25200 psi | Type I, 5 mm/min; ASTM D638 |
| 181 MPa | 26300 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 1.0 % | 1.0 % | Type I, 5 mm/min; ASTM D638 |
| 1.1 % | 1.1 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 25.08 GPa | 3638 ksi | 1 mm/min; ISO 527 |
| 26.62 GPa | 3861 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 244 MPa | 35400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 269 MPa | 39000 psi | ISO 178 | |
| Flexural Modulus | 22.5 GPa | 3260 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 23.0 GPa | 3340 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.510 J/cm | 0.955 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.99 J/cm | 7.47 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.38 | 0.38 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.39 | 0.39 | ASTM D3702 Modified |
| K (wear) Factor | 30.2 x 10-8 mm³/N-M | 15.0 x 10-10 in³-min/ft-lb-hr | Ring; ASTM D3702 Modified |
| 121 x 10-8 mm³/N-M | 60.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 0.700 µm/m-°C @Temperature -30.0 - 30.0 °C |
0.389 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 3.10 µm/m-°C @Temperature -30.0 - 30.0 °C |
1.72 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 278 °C | 532 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 279 °C @Thickness 3.20 mm |
534 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 263 °C | 505 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 267 °C @Thickness 3.20 mm |
513 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Garlock 706 Compressed Inorganic Fiber Gasketing, Nitrile Binder
- Kraton® D1160 B (SIS) Linear Triblock Copolymer
- Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, aged 16 hours at 760°C (1400°F), air cooled
- Garlock 9518 Fluoroelastomer Sheet Rubber Gasketing
- SABIC Innovative Plastics ULTEM HU1100 PEI (Asia Pacific)
- Solvay Specialty Polymers Tecnoflon® VPL 45535 Fluoroelastomer
- Solvay ALKAMULS® OR 10 Surfactant
- ChevronTexaco Clarity® ISO 320 Synthetic Paper Machine Oil
- BASF Polystyrol® 144 C Polystyrene (Europe)
- Alliance N-33 Neodymium Iron Boron Magnetic Material
Copyright © lookpolymers.com All Rights Reserved