SABIC Innovative Plastics LNP LUBRICOMP ML004LS PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP ML004LS PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* ML004LS is a compound based on Polypropylene resin containing 20% PTFE. Added features of this matLNP* Lubricomp* ML004LS is a compound based on Polypropylene resin containing PTFE. Added features of this material include: Wear Resistant, Heat Stabilized, Low Extractible.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.03 g/cc | 1.03 g/cc | ASTM D792 |
| Density | 1.03 g/cc | 0.0372 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0200 % | 0.0200 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0200 % | 0.0200 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.030 cm/cm @Time 86400 sec |
0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 16.0 MPa | 2320 psi | Type I, 5 mm/min; ASTM D638 |
| 22.0 MPa | 3190 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | 5 mm/min; ISO 527 |
| 33.0 MPa | 4790 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 28 % | 28 % | 5 mm/min; ISO 527 |
| 37.9 % | 37.9 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 5.7 % | 5.7 % | 5 mm/min; ISO 527 |
| 6.0 % | 6.0 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 1.67 GPa | 242 ksi | 1 mm/min; ISO 527 |
| 1.92 GPa | 278 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 37.0 MPa | 5370 psi | ISO 178 |
| Flexural Modulus | 1.48 GPa | 215 ksi | 2 mm/min; ISO 178 |
| 1.72 GPa | 249 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.240 J/cm | 0.450 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.65 J/cm | 10.6 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² | 16.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 3.00 J @Temperature 23.0 °C |
2.21 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.42 | 0.42 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.28 | 0.28 | ASTM D3702 Modified |
| K (wear) Factor | 14.1 x 10-8 mm³/N-M | 7.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 151 µm/m-°C @Temperature -30.0 - 30.0 °C |
83.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 141 µm/m-°C @Temperature -30.0 - 30.0 °C |
78.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C | 199 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 116 °C @Thickness 3.20 mm |
241 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 60.0 °C @Thickness 3.20 mm |
140 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Polykemi AB POLYelast TPE Z700 Thermoplastic Elastomer, SEBS-based
- NOVA Chemicals Gedexcel® 45XA Expandable Polystyrene
- Plastcom SLOVAMID 6 GF 25 FRA 5 LS PA6, 25% glass fibre, flame retardant
- Polimeri Europa Extir® F 1111 Expandable Polystyrene (discontinued **)
- LG Chemical SEETEC BS500 LDPE
- Suzhou Hipro Polymers Hiprolon® 70 NN Nylon 610, conditioned
- DSM Stanyl® TW371 Nylon 46 (European and Asian Grade) (Dry)
- ExxonMobil Exxtral™ BMV 102W Performance Polyolefin
- ExxonMobil Socony Oven Conveyor Lubricant
Copyright © lookpolymers.com All Rights Reserved