SABIC Innovative Plastics LNP LUBRICOMP KL004XXC Acetal Copolymer

Category	Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP LUBRICOMP
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP LUBRICOMP KL004XXC Acetal Copolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP LUBRICOMP* KL004XXC is a compound based on Acetal Copolymer resin containing 20% PTFE. Added feature of this material is: Wear Resistant.

Physical Properties	Metric	English	Comments
Density	1.50 g/cc	0.0542 lb/inÂ³	ASTM D792
	1.50 g/cc	0.0542 lb/inÂ³	ISO 1183
Moisture Absorption	0.150 %	0.150 %	50% RH, 24 hrs; ASTM D570
	0.260 %	0.260 %	23Â°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow	0.0197 - 0.025 cm/cm @Time 86400 sec	0.0197 - 0.025 in/in @Time 24.0 hour	ASTM D955
	0.0197 - 0.025 cm/cm @Time 86400 sec	0.0197 - 0.025 in/in @Time 24.0 hour	ISO 294
Linear Mold Shrinkage, Transverse	0.0197 - 0.025 cm/cm @Time 86400 sec	0.0197 - 0.025 in/in @Time 24.0 hour	ASTM D955
	0.0197 - 0.025 cm/cm @Time 86400 sec	0.0197 - 0.025 in/in @Time 24.0 hour	ISO 294

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	46.0 MPa	6670 psi	ISO 527
	50.0 MPa	7250 psi	ASTM D638
Tensile Strength, Yield	47.0 MPa	6820 psi	ISO 527
	51.0 MPa	7400 psi	ASTM D638
Elongation at Break	17.9 %	17.9 %	ASTM D638
	22.7 %	22.7 %	ISO 527
Elongation at Yield	9.6 %	9.6 %	ISO 527
	11.2 %	11.2 %	ASTM D638
Tensile Modulus	2.13 GPa	309 ksi	50 mm/min; ASTM D638
	2.40 GPa	348 ksi	1 mm/min; ISO 527
Flexural Strength	75.0 MPa	10900 psi	ASTM D790
	79.0 MPa	11500 psi	ISO 178
Flexural Modulus	2.06 GPa	299 ksi	ASTM D790
	2.60 GPa	377 ksi	ISO 178
Izod Impact, Notched	0.420 J/cm	0.787 ft-lb/in	ASTM D256
Izod Impact, Unnotched	6.51 J/cm	12.2 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	4.00 kJ/mÂ²	1.90 ft-lb/inÂ²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	45.0 kJ/mÂ²	21.4 ft-lb/inÂ²	80104; ISO 180/1U
Dart Drop, Total Energy	6.00 J	4.43 ft-lb	Instrumented Impact Energy @ peak; ASTM D3763
Coefficient of Friction, Dynamic	0.30	0.30	ASTM D3702 Modified
Coefficient of Friction, Static	0.18	0.18	ASTM D3702 Modified
K (wear) Factor	20.1 x 10^-8 mmÂ³/N-M	10.0 x 10^-10 inÂ³-min/ft-lb-hr	Washer; ASTM D3702 Modified

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	110 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	61.1 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
	110 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	61.1 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
CTE, linear, Transverse to Flow	111 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	61.7 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
	111 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	61.7 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	157 Â°C @Thickness 3.20 mm	315 Â°F @Thickness 0.126 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	98.0 Â°C	208 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
	99.0 Â°C @Thickness 3.20 mm	210 Â°F @Thickness 0.126 in	unannealed; ASTM D648