SABIC Innovative Plastics LNP LUBRICOMP KG002 Acetal Copolymer (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP KG002 Acetal Copolymer (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* KG002 is a compound based on Acetal Copolymer containing Graphite. Added features include : Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ISO 1183 |
| Water Absorption | 0.31 % @Time 86400 sec |
0.31 % @Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.020 cm/cm | 0.020 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 53.0 MPa | 7690 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 53.0 MPa | 7690 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 5.1 % | 5.1 % | 5 mm/min; ISO 527 |
| Elongation at Yield | 5.1 % | 5.1 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 3.40 GPa | 493 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 86.0 MPa | 12500 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 3.10 GPa | 450 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² | 19.0 ft-lb/in² | 80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.56 | 0.56 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.44 | 0.44 | ASTM D3702 Modified |
| K (wear) Factor | 207 x 10-8 mm³/N-M | 103 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 139 °C | 282 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- Nabaltec NABALOX® NO 313 Ground Alumina
- Petroquimica Triunfo Trithene® CX 7065 LDPE - Extrusion Coating
- Chevron Phillips Marlex® CL-200YNR JN (Natural) Rotational molding crosslinkable high density polyethylene (d
- SABIC Innovative Plastics LNP LUBRICOMP OCL36 PPS - Linear (Asia Pacific)
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane, 285ºF Cure Temperature
- Cytec (Conap) FR-1046 / EA-117 Conapoxy® Resin / Conacure® Hardener
- Chosun Refractories CTL AM-1 Monolithic Refractories for Ladle and Tundish
- DuPont Performance Polymers Delrin® 300TE BK602 Acetal (POM) (Unverified Data**)
- Arkema Group Pebax® 7233 SN 01 Polyether Block Amide (PEBA) (Conditioned)
Copyright © lookpolymers.com All Rights Reserved