Styrolution Styrolux® 3G46 SBC
| Category | Polymer , Thermoplastic , Styrene-Butadiene , Styrene-Butadiene Copolymer, SBC |
| Manufacturer | Styrolution |
| Trade Name | Styrolux® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution Styrolux® 3G46 SBC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Styrolux® 3G 46 is a clear styrene-butadiene copolymer (SBC) developed specifically for sheet- and film extrusion and for thermoformed articles. Styrolux® 3G 46 is designed for improved performance in blends with general-purpose polystyrene, providing parts with an excellent balance of transparency and toughness. Suggested applications: Include the whole array of food and non-food packaging like blister packs, drink cups, caps and lids, deli-trays and sheeting.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in³ | ISO 1183 |
| Water Absorption | 0.070 % | 0.070 % | |
| Linear Mold Shrinkage, Flow | 0.01651 cm/cm | 0.01651 in/in | ASTM D955 |
| Melt Flow | 11 g/10 min | 11 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 75 | 75 | ASTM D2240 |
| Tensile Strength, Yield | 25.5 MPa | 3700 psi | 2in/min; ASTM D638 |
| Elongation at Break | 220 % | 220 % | ASTM D638 |
| Tensile Modulus | 1.64 GPa | 238 ksi | 2in/min; ASTM D638 |
| Flexural Strength | 27.2 MPa | 3950 psi | ASTM D790 |
| Flexural Modulus | 1.33 GPa | 193 ksi | ASTM D790 |
| Izod Impact, Notched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | ISO 180 |
| Dart Drop, Total Energy | 20.0 J | 14.8 ft-lb | Total; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 72.0 µm/m-°C | 40.0 µin/in-°F | ASTM E831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 76.0 °C | 169 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ASTM D648 |
| Vicat Softening Point | 88.0 °C @Load 1.02 kg, Temperature 120 °C |
190 °F @Load 2.25 lb, Temperature 248 °F |
ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.572 | 1.572 | ASTM D542 |
| Haze | 0.20 % | 0.20 % | ASTM D1003 |
| Transmission, Visible | 91 % | 91 % | ASTM D1003 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | ASTM D257 |
| Dielectric Constant | 2.5 @Thickness 1.00 mm, Frequency 1.00e+6 Hz |
2.5 @Thickness 0.0394 in, Frequency 1.00e+6 Hz |
ASTM D150 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 190 - 230 °C | 374 - 446 °F | Extrusion |
| 180 - 250 °C | 356 - 482 °F | Injection | |
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Commercial Status | North America |
Users viewing this material also viewed the following:
- Permabond 932 Cyanoacrylate
- Lushan PF-3 Adhesive Resin for Coextruded Multi-layer Barrier Packaging Film
- UBE UMERIT 2000F Metallocene LLDPE
- Washington Penn Homopolymer Polypropylene 50% Talc Filled
- UBE UBESTA® 3030U Nylon 12 (After Sulfuric Acid (10%) for 500 hours)
- Covestro Makrolon® 3100 Polycarbonate
- Aremco Quartz-Coat™ 850 High Temperature Specialty Coatings Inorganic, Glass-Ceramic Filled
- Toho Tenax Besfight® G30-500 12K HTA-7S F202 Continuous Filament Carbon Fiber
Copyright © lookpolymers.com All Rights Reserved